为了解决用直流等离子体喷射法制备金刚石膜在脱膜过程中膜体开裂的问题,本文对3组脱膜开裂的金刚石膜组织结构进行了分析,发现由热应力作用产生的裂纹形貌随沉积温度的不同而呈现网状、河流状和环状,裂纹尖端的膜体具有最小的Raman 谱峰半高宽值.在所研究的温度范围内,膜体断口都是穿晶断裂和沿晶断裂的混合断口,而且断口面中的占优晶面都是{111}晶面.X射线和Raman谱结果还表明沉积温度愈高,膜体中的残余应力愈大.
参考文献
| [1] | Telling R H;Field J E .Fracture in CVD Diamond[J].International Journal of Refractory Metals and Hard Materials,1998,16:269. |
| [2] | Lu F X;Fu Y L;Zhong G F et al.A New Type of DC Arc Plasma Torch for Low Cost Large Area Diamond Deposition[J].Diamond and Related Materials,1998,7:733. |
| [3] | Ando Y;Yokota Y;Tachibana T et al.Large Area Deposition of (110)-textured Diamond Films by a 60kW Microwave Plasma CVD Reactor[J].Diamond and Related Materials,2002(11):596. |
| [4] | Yu J;Huang R F;Wen L S et al.Large Area Diamond Films Growth in Multi-filament Chemical Vapor Deposition[J].Materials Science and Engineering,1999,B57:255. |
| [5] | Rozbicki R T;Sarin V K .A Technique for Large Area Deposition of Diamond Via Combustion Flame Synthesis[J].Thin Solid Films,1998,332:87. |
| [6] | Lu F X;Tang W Z;Huang T B et al.Large Area High Quality Diamond Film Deposition by High Power DC Arc Plasma Jet Operating at Gas Recycling Mode[J].Diamond and Related Materials,2001,10:1551. |
| [7] | Vasil'ev V.V. .Investigation of plasma jet gas-dynamic effect on a substrate in conditions of diamond coating synthesis[J].Diamond and Related Materials,1999(2 Mar):202-206. |
| [8] | Kosky P G;Anthorry T R .Fracture-free Release of CVD Diamond[J].Diamond and Related Materials,1996,5:1313. |
| [9] | Vlasov II.;Obraztsova ED.;Smolin AA.;Konov VI.;Ralchenko VG. .ANALYSIS OF INTRINSIC STRESS DISTRIBUTION IN GRAINS OF HIGH DUALITY CVD DIAMOND FILM BY MICRO-RAMAN SPECTROSCOPY[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,1997(0):168-172. |
| [10] | Gu CZ.;Lu XY.;Jin ZS.;Sun Y. .The preparation of (001) textured diamond films with large areas[J].Surface & Coatings Technology,2001(0):698-701. |
| [11] | RALCHENKO V G;Smolin A A;Pereverzev V G et al.Diamond Deposition on Steel with CVD Tungsten Intermediate Layer[J].Diamond and Related Materials,1995,4:754. |
| [12] | Park D W;Yun J S .Structural Characterization of Diamond Thin Films Prepared by Plasma Jet[J].Thin Solid Films,1999,345:60. |
| [13] | Chow L.;Kleckley S.;Schulte A.;Casey K.;Wang H. .DIAMOND NUCLEATION ON GRAPHITE SUBSTRATE USING A PURE HYDROGEN FEED[J].Solid State Communications,1995(12):999-1002. |
| [14] | Jeong H J;Lee S Y;Lee W S et al.Mechanical Analysis for Crack-free Release of Chemical-vapor-deposited Diamond Wafers[J].Diamond and Related Materials,2002,11:1597. |
| [15] | 蒋正 .[D].北京科技大学,2000. |
| [16] | Kuo CT.;Lin CH.;Lu TR.;Sung CM.;Wu JY. .Internal stresses and microstructures of commercial thick diamond films deposited by different deposition methods[J].Materials Chemistry and Physics,2001(2):114-120. |
| [17] | Ager J W;Veirs K D;Rosenblatt G .Spatially Resolved Raman Studies of Diamond Films Grown by Chemical Vapor Deposition[J].Physical Review B,1991,43:6491. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%