采用适当MgO-Al比例物料,压制成型后放入气氛炉中于1500℃烧制6h,最终在样块表面得到 MgO晶须.晶须的物相组成为方镁石,显微结构研究表明多数呈细长的柱状,顶端尖锐,长约600～800μm ,长径比100～200;晶须发育的纹理特征有多种,晶须的横截面有扁六边形、正六边形、菱形和正四边形以及不规则形状等多种,能谱分析表明晶须的形貌与化学组成有关.
参考文献
| [1] | 周相廷;张兴利;陈汝芬 等.氧化镁晶须的制备[J].河北师范大学学报(自然科学版),1997,21(01):76-82. |
| [2] | Yamada;Masaharu .Apparatus for Whisker Growth[P].JP:03159999 |
| [3] | Metushevskii A S .Kinetics of Magnesium Oxide Crystal Whisker Growth during the Reaction of Magnesium Oxide with Aluminum[J].Tr Mosk Khim-Tekhnol Inst Mendeleeva,1973,72:105-107. |
| [4] | Wolff E G;Coskren T D .Growth and Morphology of Magnesium Oxide Whiskers[J].Journal of the American Ceramic Society,1956,48(06):279-285. |
| [5] | Metushevskii A S.Magnesium Oxide Whiskers and Their Properties[J].Fizika I Khimiya Obrabotki Materialov,1975(01):54-56. |
| [6] | Marshall Norwalk H .Method of Making Magnesium Oxide Fibers[P].US:3371993,1968. |
| [7] | Akira;Yamaguchi;Shinobu Hashimoto .Growth of Magnesia Whiskers[J].Ceramics International,1992,18:301-305. |
| [8] | 吴华武;张克钅宏 .制备氧化镁晶须的工艺和设备[J].功能材料,1995,26(02):177-179. |
| [9] | 袁建君.溶胶凝胶法制备的莫来石晶须的形貌和生长过程研究[J].人工晶体学报,1996(01):49. |
| [10] | 李君;赵海雷;张梅 .用C还原法制备MgO晶须的热力学分析与实验验证[J].陶瓷学报,1997,18(02):106-108. |
| [11] | 王启宝.多节状SiC晶须的VS生长机理及晶体缺陷分析[J].人工晶体学报,1997(02):180. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%