在LiNbO3晶体中掺入In2O3和Er2O3,利用提拉法生长了In:Er:LiNbO3晶体,获得了In和Er在晶体中的分凝系数.通过测试晶体的吸收光谱和抗光损伤能力,确定In:Er:LiNbO3晶体中In的掺杂阈值浓度为~3mol%,In(3mol%):Er:LiNbO3晶体的抗光损伤能力比Er:LiNbO3提高3个数量级以上.研究了In的掺入使Er:LiNbO3晶体的吸收边移动和抗光损伤能力提高的机理.
参考文献
[1] | 李铭华;杨春晖;徐玉恒.光折变晶体材料科学导论[M].北京:科学出版社,2003:143-145. |
[2] | 张福学;孙慷.压电学[M].北京:国防工业出版社,1984:158. |
[3] | Brinkmann R.;Sohler W. .Continuous-wave erbium-diffused LiNbO/sub 3/ waveguide laser[J].Electronics Letters,1991(5):415-417. |
[4] | Huang Chi-hung;McCaughan Leon .980-mm-pumped Er-doped LiNbO3 Waveguide Amplifiers: A Comparison with 1484nm Pumping[J].IEEE Journal of Selected Topics in Quantum Electronics,1996,2(02):367-372. |
[5] | Huang Chi-hung;McCaughan L .Photorefractive-damage-resistant Er-inliffused MgO:LiNbO3 ZnO-waveguide Amplifyiers and Lasers[J].Electronics Letters,1997,33(19):1639-1640. |
[6] | ZHONG Giguo;Jin Jian;Wu Zhongkang.11th Intemational Quantum Electronics Conference[J].IEEE cat No 80 CH1561-0 NewYork,1980:631. |
[7] | XU WUSHENG;WANG RUI;ZHEN XIHE .Photodamage Resistance Properties and Application of In:LiNbO_3[J].Ferroelectrics: Letters Section,2001(1/4):153-159. |
[8] | Ashkin A;Bord G D;Dziedzie J M;Smith R G, et al.Optically-induced Refractive Index Inhomogeneities in LiNbO3[J].Applied Physics Letters,1966,9(01):72-74. |
[9] | Zhen XH.;Zhao LC.;Xu YH. .Defect structure and optical damage resistance of Zn : Fe : LiNbO3 crystals[J].Applied physics, B. Lasers and optics,2003(6):655-659. |
[10] | SWEENEY K L;Halliburton L E;Bryan D A .Point Defects in Mg-doped Lithium Niobate[J].Journal of Applied Physics,1985,57(04):1036-1038. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%