分别采用K2O助溶剂提拉法和富锂提拉法生长了近化学计量比LiNbO3晶体.比较了两种方法生长的晶体紫外吸收边和红外吸收谱的差别,光谱结果表明,K2O助溶剂提拉法生长的晶体组成非常均匀,而富锂提拉法生长的晶体组成不均匀,沿晶体生长方向,Li2O含量逐渐增加.另外,两种生长方法中,籽晶表面均看到螺旋状环,分析了其产生原因.
参考文献
| [1] | 孙敦陆,杭寅,张连瀚,钱小波,李世峰,徐军,罗国珍,祝世宁,朱永元,周圣明.化学计量比LiNbO3晶体的畴结构及完整性研究[J].人工晶体学报,2002(04):387-391. |
| [2] | 王海丽,杭寅,张连瀚,祝世宁,徐军.掺镁近化学计量比LiNbO3晶体的生长[J].无机材料学报,2004(05):1191-1194. |
| [3] | Gopalan V.;Furukawa Y.;Kitamura K.;Mitchell TE. .The role of nonstoichiometry in 180 degrees domain switching of LiNbO3 crystals[J].Applied physics letters,1998(16):1981-1983. |
| [4] | Kitamura K;Yamamoto J K;Iyi N et al.Stoichiometric LiNbO3 Single Crystal Growth by Double Crucible Czochralski Method Using Automatic Powder Supply System[J].Journal of Crystal Growth,1992,116:327. |
| [5] | Bermudez V;Dutta P S;Serrano M D et al.Effect of Crystal Composition on the Domain Structure of LiNbO3 Grown from Li Rich Melts by the Czochralski Technique[J].Journal of Crystal Growth,1997,172:269. |
| [6] | 陈晓军,李兵,朱登松,李冠告,陈绍林,黄自恒,吴仲康.近化学计量比LiNbO3晶体的生长及其组分测定[J].人工晶体学报,2001(02):129-134. |
| [7] | Bermudez V;Dutta PS;Serrano MD;Dieguez E .On the single domain nature of stoichiometric LiNbO3 grown from melts containing K2O[J].Applied physics letters,1997(6):729-731. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%