本文研究了在430℃,填充度为35用了3mol/L,5mol/L LiOH做矿化剂,所获得晶体均为10μm以下的微晶.当矿化剂为1mol/L LiOH和1mol/L KBr时,所获得晶体同样为几微米的微晶,显露完整的正极面{0001}、负极面{0001}、锥面{1011}和柱面{1010}.矿化剂为3M LiOH和3M KBr时,出现个体较大的晶体,直径超过100μm,显露正极面{0001}、正锥面{1011}和柱面{1010},负极面出现缺损现象.由此说明和K+相比溶液中的Li+不利于生成大尺寸ZnO晶体.
参考文献
| [1] | Bagnall DM;Chen YF;Zhu Z;Yao T;Koyama S;Shen MY;Goto T .Optically pumped lasing of ZnO at room temperature[J].Applied physics letters,1997(17):2230-2232. |
| [2] | Zu P.;Wong GKL.;Kawasaki M.;Ohtomo A.;Koinuma H.;Segawa Y.;Tang ZK. .ULTRAVIOLET SPONTANEOUS AND STIMULATED EMISSIONS FROM ZNO MICROCRYSTALLITE THIN FILMS AT ROOM TEMPERATURE[J].Solid State Communications,1997(8):459-463. |
| [3] | Bagnall DM.;Zhu Z.;Yao T.;Shen MY.;Goto T.;Chen YF. .High temperature excitonic stimulated emission from ZnO epitaxial layers[J].Applied physics letters,1998(8):1038-1040. |
| [4] | 郭常新,傅竹西,施朝淑.阴极射线激发下ZnO薄膜室温紫外发光的超线性增长规律[J].发光学报,1998(03):239-241. |
| [5] | 吕树臣,宋国利,肖芝燕,张家骅,黄世华.纳米氧化锌粉体的制备及发光性质的研究[J].发光学报,2002(03):306-310. |
| [6] | N. Y. Garces;L. Wang;L. Bai;N. C. Giles;L. E. Halliburton;G. Cantwell .Role of copper in the green luminescence from ZnO crystals[J].Applied physics letters,2002(4):622-624. |
| [7] | 井立强,徐自力,孙晓君,尚静,蔡伟民,杜尧国,傅宏刚.ZnO和TiO2粒子的光催化活性及其失活与再生[J].催化学报,2003(03):175-180. |
| [8] | 井立强,郑莹光,徐自力,董凤霞,孙晓君,蔡伟民,徐英凯.ZnO超微粒子的EPR特性和光催化性能[J].高等学校化学学报,2001(11):1885-1888. |
| [9] | 井立强,徐自力,杜尧国,孙晓君,王玲,周秀清,单洪岩,蔡伟民.ZnO超微粒子光催化氧化降解n-C7H16的研究[J].高等学校化学学报,2002(05):871-875. |
| [10] | 杨青林,郭林,吴中华,江雷,徐文国,李前树.室温下纳米氧化锌新相的合成及表征[J].高等学校化学学报,2003(01):82-85. |
| [11] | 王振旅,马红超,朱万春,于剑锋,王国甲.在纳米Cu-ZnO上仲丁醇的催化脱氢[J].高等学校化学学报,2002(11):2163-2165. |
| [12] | 丁士文,张绍岩,刘淑娟,丁宇,康全影,刘燕朝.直接沉淀法制备纳米ZnO及其光催化性能[J].无机化学学报,2002(10):1015-1019. |
| [13] | 李旦振,陈亦琳,林熙,王绪绪,付贤智.纳米ZnO的制备及发光特性研究[J].无机化学学报,2002(12):1229-1232. |
| [14] | 华素坤.热液条件下ZnO晶体的形成机理[J].人工晶体学报,1994(03):177. |
| [15] | 王步国.ZnO晶体的极性生长习性与双晶的形成机理[J].人工晶体学报,1997(02):102. |
| [16] | 张军,孙聆东,廖春生,严纯华.氧化锌微晶的制备和形貌控制[J].无机化学学报,2002(01):72-74. |
| [17] | 李汶军;施尔畏;田明原 等.水热法制备氧化锌纤维基纳米粉体[J].中国科学E辑,1998,28(03):212-219. |
| [18] | Liu B;Zeng H C .Hydrothermal Synthesis of ZnO Nanorods in the Diameter Regime of50nm[J].Journal of the American Chemical Society,2003,125(15):4430-4431. |
| [19] | Guo L Ji L;Xu H et al.Regularly Shaped, Single-crystalline ZnO Nanorods with Wurtzite Structure[J].Journal of the American Chemical Society,2002,124(50):14864-14865. |
| [20] | Urbieta A.;Piqueras J.;Hardalov C.;Sekiguchi T.;Fernandez P. .Cathodoluminescence microscopy of hydrothermal and flux grown ZnO single crystals[J].Journal of Physics, D. Applied Physics: A Europhysics Journal,2001(19):2945-2949. |
| [21] | Sekiguchi T.;Obara K.;Shishido T.;Sakagami N.;Miyashita S. .Hydrothermal growth of ZnO single crystals and their optical characterization[J].Journal of Crystal Growth,2000(0):72-76. |
| [22] | Eriko Ohshima;Hiraku Ogino;Ikuo Niikura;Katsumi Maeda;Mitsuru Sato;Masumi Ito;Tsuguo Fukuda .Growth of the 2-in-size bulk ZnO single crystals by the hydrothermal method[J].Journal of Crystal Growth,2004(1/2):166-170. |
| [23] | 董国义,韦志仁,林岩,王立明,李志强,张华伟.水热法合成氧化锌晶体[J].人工晶体学报,2003(02):130-133. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%