由于与GaN晶格失配小(约1.4%),γ-LiAlO2单晶有望成为GaN外延衬底材料.本文首先使用提拉法生长出了尺寸达φ45×50mm3的γ-LiAlO2单晶,然后采用Ga2O3作为掺杂剂,仍用提拉法生长出了三种不同掺镓浓度的LiAl1-xGaxO2(x=0.1,0.2,0.3)晶体,并用X射线粉末衍射(XRPD)分别对晶体及坩锅中剩余的熔体的成份进行了表征.结果表明LiAl-xGaxO2(x=0,0.1,0.2,0.3)晶体归属于γ-LiAlO2结晶结构,Ga3+离子部分地取代Al3+离子,发生分凝且分凝系数小于1.
参考文献
| [1] | Ponce F A;Bour D P .Nitride-based Semiconductors for Blue and Green Light-emitting Devices[J].Nature,1997,386:351-359. |
| [2] | Liu L.;Edgar JH. .Substrates for gallium nitride epitaxy [Review][J].Materials Science & Engineering, R. Reports: A Review Journal,2002(3):61-127. |
| [3] | Xu Ke;Xu Jun;Deng Peizhen;Zhou Yongzong, Zhou Guoqing, Qiu Rongsheng, Fang Zujie .γ-LiAlO2 Single Crystal: a Novel Substrate for GaN Epitaxy[J].Journal of Crystal Growth,1998,193:127-132. |
| [4] | WALTEREIT P;Brandt O;Trampert A;Grahn H T, Menniger J, Ramsteiner M, Reiche M, Ploog K H .Nitride Semiconductors Free of Electrostatic Fields for Efficient White Light-emitting Diodes[J].Nature,2000,406:865-868. |
| [5] | Waltereit P.;Ramsteiner M.;Trampert A.;Grahn HT.;Menniger J.;Reiche M.;Ploog KH.;Brandt O. .M-plane GaN(1(1)over-bar-00) grown on gamma-LiAlO2(100): nitride semiconductors free of internal electrostatic fields[J].Journal of Crystal Growth,2001(0):437-441. |
| [6] | WALTEREIT P;Brandt O;Ramsteiner M;Uecker R, Reiche P. Ploog K H .Growth of M-plane GaN on γ-LiAlO2 ( 100 )[J].Journal of Crystal Growth,2000,218:143. |
| [7] | Cockayne B;Lent B .The Czochralski Growth of Single Crystal Lithium Aluminate, LiAlO2[J].Journal of Crystal Growth,1981,54:546. |
| [8] | Kung P;Saxler A;Zhang X;Walker D, Lavado R, Razeghi M .Metalorganic Chemical Vapor Deposition of Monocrystalline GaN Thin Films on β-LiGaO2 Substrates[J].Applied Physics Letters,1996,69:2116. |
| [9] | Takao Ishii;Yasuo Tazoh;Shintaro Miyazawa .LiGaO2 Single Crystals for a Substrate of Hexagonal GaN Thin Films[J].Japanese Journal of Applied Physics,1997,36:139. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%