本文采用机械合金化法成功制备了N型赝三元(Bi2Te3-Sb2Te3-Sb2Se3)合金粉体材料,该材料颗粒均匀、细小,颗粒尺寸在10~100nm量级.在此基础上采用冷压烧结法制备了N型赝三元机械合金化冷压烧结热电材料.研究了这种热电材料的电导率、塞贝克系数与烧结温度的关系.

参考文献

[1] Yim W M;Rosi F D .Compound Telluride and Their Alloys for Peltier Cooling-a Revier[J].Journal of Solid State Electron,1972,15:1121.
[2] Row D R.Handdook of Thermoelectrics[M].CRC Press:Boca Raton,FL,1995:597.
[3] Gerald Mahan;Brian Sales;Jeff Sharp .THERMOELECTRIC MATERIALS: NEW APPROACHES TO AN OLD PROBLEM[J].Physics Today,1997(3):42-47.
[4] Wyckoff R W G.Crystal Structure[M].Interscience Publishers,New York,1964
[5] Row D M .[J].Applied Energy,1986,24:139.
[6] Yanagitani A;Nishikawa S;Tanaka Y.Characteristics of Bi2Te3 Compound Produced by Rapid Solidification[A].Yokohama,1993:277.
[7] 荣剑英.大尺寸(Bi2Te3)0.90(Sb2Te3)0.05(Sb2Se3)0.05晶体的生长及性能[J].人工晶体学报,1997(03):311.
[8] Hyun DB.;Oh TS.;Shim JD.;Kolomoets NV.;Hwang JS. .Electrical properties of the 85% Bi2Te3 15% Bi2Se3 thermoelectric material doped with SbI3 AND CuBr[J].The journal of physics and chemistry of solids,1998(6/7):1039-1044.
[9] 郎荣福,荣剑英,赵秀平,李将录,赵洪安.大尺寸赝三元半导体致冷材料的制备与性能[J].人工晶体学报,2002(02):144-147.
[10] Koukharenko E;Frety N;Shepelerich V G;Tedenac J C .Thermoelectric Properties of Bi2Te3 Materials Obtained by the Ultrarapid Quenching Process Route[J].J Alloys Comp,2000,299(1-2):254.
[11] Yang J.;AizaWa T. .Thermoelectric properties of p-type (Bi_2Te_3 )_x(Sb_2Te_3)_(1-x) prepared via bulk mechanical alloying and hot pressing[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2000(1/2):225-228.
[12] 吕强,胡建民,信江波,荣剑英.N型赝三元热压热电材料的微观结构和电学性能[J].人工晶体学报,2004(05):788-791.
[13] 胡淑红;赵新兵;朱铁军;邬震泰,周邦昌 .Bi2Te3和Bio 5Sb1.5Te3的机械合金化法制备及其热电性能[J].中国有色金属学报,2000,10(增刊):73-76.
[14] Hasezaki K;Nishimura M et al.Mechannical Alloying of BiTe and BiTeSb Thermoelectric Material[J].Materials Transactions JIM,1994,35(06):428-432.
[15] SJ 2857-1988.SJ 2857-1988.国家电子工业部标准[S].
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%