用电子探针、X射线衍射仪等设备研究了商用铌铁铸锭中的相.研究结果表明,合金中存在Fe2Nb、FeNb以及Fe2Nb3相.在不同牌号的铌铁合金中,各相的成分都不同程度地偏离了其原子配比.铸锭中亚稳Fe2Nb3相的存在是由于凝固过程溶质元素以及杂质原子在凝固前沿富集的必然结果,也与其晶体结构有关.
参考文献
| [1] | 雍岐龙;裴和中;田建国 等.铌在钢中的物理冶金学基础数据[J].钢铁研究学报,1998,10(02):66-69. |
| [2] | Okamoto H .Fe-Nb[J].Journal of PHASE EQUILIBRIA,1993,14:650-652. |
| [3] | Bejarano J M Z;Gama S;Ribeiro C A .The Iron Niobium Phase Diagram[J].Zeitschrift fur Metallkunde,1993,84:160-164. |
| [4] | Okamoto H .Fe-Nb[J].Journal of Phase Equilibria,2002,23:112. |
| [5] | Srikanth S;Petric A .A Thermodynamic Evaluation of the Fe-Nb System[J].Zeitschrift fur Metallkunde,1994,85:164-170. |
| [6] | Okamoto H .Comment on FeNb[J].Journal of Phase Equilibria,1995,16:369-370. |
| [7] | Goldschmidt H J .[J].Journal of the Iron and Steel Institute,1960,194:160. |
| [8] | Kubaschewski O.Iron-Binary Phase Diagrams[M].Springer Verlag,Berlin,1982 |
| [9] | Bejarano J M Z;Gama S;Ribeiro C A .On the Existence of Fe2Nb3 Phase[J].Zeitschrift fur Metallkunde,1991,82:615-620. |
| [10] | Schon C G;Tenorio J A S .The Chemistry of the Iron-Niobium Intermetallics[J].Intermetallics,1996,4:211-216. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%