用扫描电镜研究了铸造铝硅合金表面浸锌膜的形貌,用电子探针、能谱仪研究了浸锌薄膜的组成,用增重法测试了浸锌膜的重量.结果表明,硫酸锌的含量对浸锌膜的形貌有较大影响,随浸锌时间的增加,锌膜趋于均匀化,第二次浸锌20～30 s,锌膜可以均匀地覆盖整个基体表面.浸锌膜中主要成分是锌,其次为铁、镍、铜.第一次浸锌30 s时,膜重达到最大值.
参考文献
| [1] | Stoyanova E;Stoychev D .Electrochemical Aspects of the Immersion Treatment of Aluminum[J].Journal of Applied Electrochemistry,1997,27:684-689. |
| [2] | Robertson SG.;Druskovich DM.;Ritchie IM. .A KINETIC AND ELECTROCHEMICAL STUDY OF THE ZINCATE IMMERSION PROCESS FOR ALUMINIUM[J].Journal of Applied Electrochemistry,1995(7):659-666. |
| [3] | Court S.W.;Barker B.D. .Electrochemical Measurements of Electroless Nickel Coatings on Zincated Aluminium Substrates[J].Transactions of the Institute of Metal Finishing,2000(4):157-162. |
| [4] | Yee Chin Tang;Alison J Davenport .The Effect of Heat Treatment and Surface Roughness on the Zincate Treatment of Aluminum Alloy 6082[J].Transactions of the Institute of Metal Finishing,2001,79(03):85-89. |
| [5] | Pearson T;Wake S .Verbesserungen bei der Vorbehandlung von Aluminium als Substratfuerdie galvanische Abscheidung[J].GALVANOTECHNIK,2000,91(11):3054-3061. |
| [6] | 杨贤金;崔振铎.纯铝表面浸锌薄膜的研究[J].物理测试,1995(03):25-28. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%