在Gleeble 1500热模拟机上测定了温度为850℃,变形为50%的单道次及多道次动态CCT曲线,并以此为依据在Ar3附近进行了多道次积累大变形和单道次大变形的轧制对比实验.同时进行了变形温度、变形量和冷却速度对铁素体相变行为的影响研究.结果发现在奥氏体未再结晶区进行多道次大压下量轧制及轧后快速冷却,可以大大地细化晶粒.
参考文献
[1] | Redko Kaspar;Ulrich Lotter;Christian Biegus .The Influence of Thermomechanical Treatment on the Transformation Behavoir of Steels[J].Steel Research International,1994,65(06):242. |
[2] | Wung Yong Choo.ferrite Refinement Through heavy Deformation InPlanin Low carbon steel[J].CAMP-JSIJ,1999(12):369. |
[3] | Kepima;Yoshiyuki Watanable;Yoshio Terada .atsuhiko Yoshie and Hiroshi Tamehior.Ferrite Grain Refinement by Large Reduction per Pass inj Non-recrystallization Temperature Region of Austenite[J].ISIJ International,1996,36(05):6301. |
[4] | Yoshikazu Matumura;Hiroshi Yada .Evolution of ultrafine-grainer Ferrite in Hot Successive Deformation[J].Transactions of the Iron and Steel Institute of Japan,1987,27:492. |
[5] | Minoru Umemoto.hideyuki Ohtsuka,Imao Tamura.Transformation to Pearlite From Work-hardened Austenite[J].Transactions of the Iron and Steel Institute of Japan,1983(23):775. |
[6] | Torizuka.formation of a Fine Ferrite-pearite Structure from a coarse Austenite Grain structure through heavy Deformation of Austentie followed by Contrloed Cooling[J].CAMP-JSIJ,1998(11):565. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%