在Gleeble 3800热模拟机上进行低碳Si-Mn系Q & P钢的热处理模拟,采用X射线衍射仪和透射电子显微镜研究了热处理后试样中残余奥氏体的量及其分布规律.XRD研究表明:Q & P钢中残余奥氏体的存在提高了钢的塑性;Q & P工艺中较高的配分温度和较长的配分时间可以得到较多的残余奥氏体.透射电镜观察表明Q & P钢中残余奥氏体形态有马氏体板条问条状奥氏体和晶界处块状奥氏体两种.
参考文献
| [1] | Takehide SENUMA .Physical Metallurgy of Modern High Strength Steel Sheets[J].ISIJ International,2001(6):520-532. |
| [2] | 小宫幸久.汽车用钢铁材料的现状和发展动向[J].鞍钢技术,2004(04):65-67. |
| [3] | J. Speer;D. K. Matlock;B. C. De Cooman;J. G. Schroth .Carbon partitioning into austenite after martensite transformation[J].Acta materialia,2003(9):2611-2622. |
| [4] | Speer JG;Edmonds DV;Rizzo FC;Matlock DK .Partitioning of carbon from supersaturated plates of ferrite, with application to steel processing and fundamentals of the bainite transformation[J].Current opinion in solid state & materials science,2004(3/4):219-237. |
| [5] | Speer J G;Rizzo F C;Matlock D K et al.The"quenching and partitioning"process:Background and recent progress[J].Materials Research,2005,8(04):417-423. |
| [6] | 李华瑞.材料x射线衍射分析实用方法[M].北京:冶金工业出版社,1994 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%