研究了化学镀Ni-P-B合金溶液的稳定性和镀层的结构.结果表明,增大镀液中硫酸镍、硼氢化钠、次亚磷酸钠浓度及溶液的pH值,会降低镀液的稳定性,而甲酸浓度增大则会显著改善镀液的稳定性.镀层中硼含量增加使磷含量下降,且镀层结构由非晶向微晶转变.镀层硬度随硼含量增加而增大,400 ℃热处理后镀层硬度具有最大值.