水体对金属的冲刷行为会加剧金属的腐蚀,影响金属的使用寿命,冲刷行为的腐蚀机理很复杂,不同的环境介质和不同的金属材料其腐蚀机理亦不同.弄清楚冲刷腐蚀的机理有利于金属的防腐蚀设计.为此,对冲刷腐蚀的特征、影响因素、研究方法及腐蚀机理进行了论述.
参考文献
[1] | Postlethwaite J;Tinker E B;Hawrylak M M.Erosion-Corrosion in Slurry Pipelines[J].Corrosion,1974(30):285. |
[2] | 曾德龙 .长江三峡水利枢纽金属结构腐蚀环境及设计技术研讨[J].人民长江,1985,26(ZK) |
[3] | 中国腐蚀与防护学会 .三峡工程金属结构防腐蚀问题的调查研究与分析报告[R]. |
[4] | 林海潮;裴鸿勋 .水利枢纽腐蚀情况及三峡水利工程腐蚀破坏的可能性分析[J].人民长江,1995,26(ZK) |
[5] | 张文保.试论船闸金属结构的腐蚀防护[A].宜昌,1997 |
[6] | 宜昌市环境保护监测站 .葛洲坝船闸处长江水质监测报告[R].,1995. |
[7] | Barry;Syrett .Erosion-Corrosion of Copper-Nickel Alloys in Sea Water and Other Aqueous Environments--A literature Review[J].Corrosion,1976,32(242) |
[8] | 朱日彰.腐蚀与防护技术基础[M].北京:冶金工业出版社,1987 |
[9] | 左景伊.腐蚀工程[M].北京:化学工业出版社,1987 |
[10] | Shadlec J R;Shirazi S A;Dayalan E.Erosion-Corrosion of a Carbon Steel Elbow in a Carbon Dioxide Environment[J].Corrosion,1996(52):714. |
[11] | Ellison B T;Cornet I .Mass Transfer to a Rotating Disk[J].Journal of the Electrochemical Society,1971,118(01):68-71. |
[12] | May Marie de Ficquelmont-Loizos;Luc Tamisier;AdrienCaprani .Mass Transfer in Laminar Flow at a Rotating Disk elec-trode in Suspensions of Inert Particles[J].Journal of Electrochemistry,1988,135(03) |
[13] | Zhou S;Stack M M;Newman R C .Characterization of Synergistic Effects Between Erosion and Corrosion in an Aqueous Environment Using Electrochemical Techniques[J].Corrosion,1996,52:934. |
[14] | Gilbert P T.Paper4,Consideration Affecting the Use of Copper Alloy Tubes in Distillation Plant[A].London:Copper Development Assoc,1968 |
[15] | Orava R N.Stress Corrosion and Corrosion Behavior of Copper-Nickel and Titanium under Simulated Desalination Condition[A].Houston Texas:[s.n.],1969 |
[16] | Anderson D B .Factors Affecting Corrosion of Copper and Copper Alloys in Hot Sea Water[J].Naval Engineers Journal,1965,77:470. |
[17] | Postlethwaite J;Mark W;Hawrylak .Effect of Slurry Abrasion on the Anodic Dissolution of Iron in Water[J].Corrosion,1975,31:237. |
[18] | Pitt C H;Chang Y M .Jet Slurry Corrosive Wear of High-Chromium Cast Iron and High-Carbon Alloy[J].Corrosion,1986,42(06):312-317. |
[19] | Davies D H;Burstein G T.The Effect of Bicarbonate on the Corrosion and Passivation of Iron[J].Corrosion,1980(36):416. |
[20] | Castro E B;Valentini C R;Moina C A et al.The Influence of Ionic Composition on the Electrodissolution and Passivation of Iron Electrodes in Potassium Carbonate-Bicaronate Solutions in the 8.4~10.5 pH Range At 25 ℃[J].Corrosion Science,1988,26(10):781-793. |
[21] | Oka Y;Matsumura M;Yamawaki M.Slurry Erosion-Corrosion on Commericially Pure Iron in a Vibratory Testing Facility[A].U K:Cavendish Laboratory,University of Cambridge,1987 |
[22] | Yue Z;Zhou P;Shi J.Some Factors Influencing Erasion-Corrosion Performance of Materials[A].New York:ASME,1987 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%