利用离子束混合-离子注入(Ar+)和磁控溅射相结合的实验技术在HR-1不锈钢基体上制备了注入N+的SiC涂层,并用表面分析手段对所制备涂层的表面形貌、剖面形貌、相结构、表面成分、表面元素的化学态进行了分析.结果表明:制备的涂层结构致密、表面平整、膜层成分均匀;涂层与基体之间形成了一明显的过渡层,增强了涂层和基体之间的结合力.用二次离子质谱(SIMS)对充氘涂层的阻氢性能进行了定性分析.结果表明:涂层元素与氢形成稳定的化学键,抑制了氢的扩散和迁移,使得涂层具有一定的阻氢能力.
参考文献
| [1] | Shan C Q;WU A J;Li V G et al.The behaviour of diffusion and permeation of tritium through 316L stainless steel[J].Journal of Nuclear Materials,1992,191-194:221. |
| [2] | Forcey K S;Perujo A;Reiter F et al.The formation of tritium permeation barrier by CVD with coating of TiC and TiN+TiC[J].Journal of Nuclear Materials,1993,200:417. |
| [3] | Perjo A;Forcey K S .Tritium Permeation Barriers for Fusion Technolgy[J].Fusion Engineering and Design,1995,28:252. |
| [4] | Huang Q R;Shan C Q.Tritium barrier development[A].Dayton OH:[s.n.],1994:180. |
| [5] | Elleman T S;Verghese K .The diffusion of hydrogen in SiC[J].Journal of Nuclear Materials,1974,53:299. |
| [6] | Hollenberg G W;Hollenberg R A;Josephis P H et al.The Barrier of Hydrogen on Stainless Steel[J].Fusion Engineering and Design,1995,28:190. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%