采用间歇式中性盐雾加速试验方法研究了Q235钢热镀锌及55Al-Zn合金镀层的腐蚀行为,利用扫描电镜(SEM)和能谱仪(EDS)分析了镀层的微观组织和腐蚀产物的成分.镀层的微观组织分析结果表明热镀锌层由表及里是η相(纯锌)、ζ相(FeZn13)、δ1相(FeZn7)和α固溶体组成;热镀锌铝合金镀层由两层组成,外层由富锌和富铝两相固溶体组成,内层由单一的η相(Fe2Al5)组成.盐雾试验和腐蚀产物分析结果表明,热镀锌铝合金层的耐腐蚀性能优于热镀锌层.
参考文献
| [1] | 张益明;马荣贵;符寒光 .耐蚀热镀锌钢板在汽车工业中应用的进展[J].腐蚀与防护,1999,20(11):483. |
| [2] | 顾国成;刘邦津.热浸镀[M].北京:化学工业出版社,1988 |
| [3] | 武汉材料保护研究所.钢铁化学热处理金属图谱[M].北京:机械工业出版社,1980 |
| [4] | Sere P R;Zapponi M;Elsner C I.Comparative Corrosion Behaviour of 55Aluminium-Zinc Alloy and Zinc Hot-Dip Coatings Deposited on Low Carbon Steel Substrates[J].Corrosion Science,1998(10):1711. |
| [5] | Lin K L;Yang C F;Lee J T.Correlation of Microstructure with Corrosion and Electrochemical Behavior of the Batch-Type Hot-Dip Al-Zn Coatings:part I Zn and 55%Al-Zn Coating[J].Corrosion,1991(01):9. |
| [6] | Lin K L;Yang C F;Lee J T.Correlation of Microstructure with Corrosion and Electrochemical Behavior of the Batch-Type Hot-Dip Al-Zn Coatings:part Ⅱ Zn and 55%Al-Zn Coating[J].Corrosion,1991(01):7. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%