对化学镀Ni-P-SiC复合镀层的微观组织结构特征进行了研究,结果表明,SiC微粒弥散分布在复合镀层中,Ni-P合金主要作为粘结金属包络着SiC微粒,两者之间存在电子转移,发生了界面反应,反应扩散层为10-1 nm级,界面结合紧密,无孔隙和裂纹等缺陷.元素存在形态主要表现为Ni和P以单质的形式存在,Si以共价健SiC的形式存在,Ni-Ni之间以金属键进行结合.
参考文献
| [1] | Zhu Q;Ma C;Qiu X .Oxidation resistant SiC coating for graphite materials[J].Carbon: An International Journal Sponsored by the American Carbon Society,1999(9):1475-1484. |
| [2] | Martin W Bayes .Electroless Nickel in the 90′s[J].Metal Finishing,1990,4:27. |
| [3] | Mandich N V;Krulik G A .The Evolution of a Process:Fifty Years of Electroless Nickel[J].Metal Finishing,1992,5:25. |
| [4] | ZHANG Bangwei;Hu Wangyu;Zhu Deqi .Magnetic Properties of Crystalline and Amorphous Fe-B alloys Prepared by Electroless Plating[J].Physical Review B,1993,183:205-210. |
| [5] | L. Das;D.-T. Chin .Effect of Bath Stabilizers On Electroless Nickel Deposition on Ferrous Substrates[J].Plating & Surface Finishing,1996(8):55-61. |
| [6] | 徐智谋 .化学镀SiC/Ni-P梯度镀层基础性研究[D].华中理工大学,2000. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%