开发了一种无铬无毒的环保型镀锌层钝化工艺,通过试验研究了钝化液成分和工艺条件对钝化膜的影响情况.钢铁件在锌酸盐或酸性镀锌15 μm后,采用此工艺钝化,得到的钝化膜抗白锈试验24 h,中性盐雾试验72 h达到5 级(符合国家标准),钝化液排放达到环保要求.
参考文献
[1] | 朱传芳;胡蜡生 .植酸在镀锌无铬钝化中的应用[J].精细化工,1995,12(05):12-14. |
[2] | Wilcox G D;Gabe D R .Passivation Studies Using Group VIA Anions. Part 5:Cathodic Treatment of Zinc[J].British Corrosion Journal,1987,22(04):254-256. |
[3] | Wilcox G D;Gabe D R .Passivation Studies Using Group VIA Anions. Part 4:Cathodic Treatment of Zinc[J].British Corrosion Journal,1984,19(04):196-198. |
[4] | Bijimi D;Gabe D R .Passivation Studies Using Group VIA Anions. Part 1:Anodic Treatment of Zinc[J].British Corrosion Journal,1983,18(02):88-91. |
[5] | Bijimi D;Gabe D R .Passivation Studies Using Group VIA Anions,Part 2:Anodic Treatment of Zinc[J].British Corrosion Journal,1983,18(02):93-95. |
[6] | Bijimi D;Gabe D R .Passivation Studies Using Group VIA AnionsPart 3:Anodic Treatment of Zinc[J].British Corrosion Journal,1983,18(03):138-140. |
[7] | Wharton J A;Wilcox G D;Baldwin K R .Non-Chromate Conversion Coating Treatments for Electrodeposited Znic-Nickel Alloys[J].Transactions of the Institute of Metal Finishing,1996,74(06):2-5. |
[8] | Tang P T;Bech-Nielson G Moller .Molybdate Based Passivation of Zinc[J].Transactions of the Institute of Metal Finishing,1997,75(04):144-146. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%