为了获得大面积有序孔排列以及不同孔径的氧化铝膜,采用二次阳极氧化法可制备大面积有序铝阳极氧化多孔(AAO)膜,着重研究氧化电压、氧化时间、电解液浓度以及扩孔时间对AAO膜孔径大小、膜层厚度和形貌结构的影响,用X射线粉末衍射(XRD)仪进行物相分析,利用扫描电子显微镜(SEM)表征多孔膜的形貌.结果表明,在700 ℃以下条件下AAO膜以无定形态存在,经800 ℃退火后无定形氧化铝转化为γ-Al2O3,多孔膜随电压和电解液浓度增加而增大,经H3PO4溶液扩孔后可获得较大孔径模板,扩孔时间与孔径变化呈近似线性关系.为满足应用需求的AAO膜的制备提供了依据.
参考文献
| [1] | 苏育志,龚克成.纳米结构材料的模板合成方法[J].材料科学与工程,1999(04):17-21. |
| [2] | Aranda P.;Garcia JM. .Porous membranes for the preparation of magnetic nanostructures[J].Journal of Magnetism and Magnetic Materials,2002(1/2):214-219. |
| [3] | Zhou YK.;Li HL. .Sol-gel template synthesis of highly ordered LiCo0.5Mn0.5O2 nanowire arrays and their structural properties[J].International Journal of Quantum Chemistry,2002(2):247-253. |
| [4] | Li L.;Zhang Y.;Li GH.;Zhang LD. .A route to fabricate single crystalline bismuth nanowire arrays with different diameters[J].Chemical Physics Letters,2003(3-4):244-249. |
| [5] | DingXJ;Zhang J Z;Wang R D .Anovelpreparationofporousaluminawithparallelchannels[J].Materials Letters,2001,51:429. |
| [6] | Li AP.;Birner A.;Nielsch K.;Gosele U.;Muller F. .Hexagonal pore arrays with a 50-420 nm interpore distance formed by self-organization in anodic alumina[J].Journal of Applied Physics,1998(11):6023-6026. |
| [7] | JEssenskyOO;MüLLERF .Self-organizedformationofhexagonalporestructuresinanodicalumina[J].Applied Physics Letters,1998,72(10):1173. |
| [8] | WangX;Han G R .Fabricationandcharacterizationofanodicaluminumoxidetemplate[J].Microelectronic Engineering,2003,66:166. |
| [9] | 韩喻,谢凯.电化学制备亚微米氧化铝有序多孔膜方法研究[J].微纳电子技术,2003(07):137-141. |
| [10] | 徐洮.铝阳极氧化膜的扩孔处理[J].材料保护,1994(09):18. |
| [11] | 徐金霞 .多孔氧化铝模板制备与纳米阵列体系组装[D].合肥工业大学,2002. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%