以往对渗铝钢耐热腐蚀性能的研究缺乏深度,为解决实际问题,在750 ℃模拟灰垢熔盐体系中,研究了加热炉辐射室炉管常用材料20G钢、20G渗铝钢、Cr5Mo钢、Cr5Mo渗铝钢的腐蚀行为.结果表明:20G钢、Cr5Mo钢、20G渗铝钢和Cr5Mo渗铝钢抗熔灰腐蚀能力依次增强;渗铝可以大大提高合金的耐熔灰腐蚀性能,在纯空气中氧化,其耐蚀性能也十分优异;20G渗铝钢在熔灰腐蚀时元素Al优先氧化并不十分明显,Cr5Mo渗铝钢在熔灰腐蚀时元素Al优先氧化;按照电化学模型,在熔灰腐蚀中V-2O-5不但会溶解金属氧化物的保护层,而且还参与阴极过程,循环反应,加速了金属的氧化腐蚀.
参考文献
| [1] | ryersRW .Firesideslagging,fouling,andhigh-temperaturecorrosionofheat-transfersurfaceduetoimpuritiesinsteam-raisingfuels[J].Progress in Energy and Combustion Science,1996,22:29. |
| [2] | ThomasWH.Inorganic Constituents of Petroleum[M].London:OxfordUniversityPress,1938 |
| [3] | owdenAT;Draper P;Rowling H.Theproblemoffueloilashdepositioninopen-cyclegasturbines[J].Proceedings of the Institution of Mechanical Engineers Part A Journal of Power and Energy,1953:167. |
| [4] | MillerPD;Slunder G J;Krause H H.Control of corrosion and deposits in stationary boilers burning residual fuel oil In[A].Navy Department,1963:5. |
| [5] | 李碚;高怀荪;江丽萍 .铈提高Fe-15Cr合金抗氧化能力的作用机理[J].中国腐蚀与防护学报,1986,6(03):205. |
| [6] | 张允书 .热腐蚀的盐溶机理及其局限性[J].中国腐蚀与防护学报,1987,12(01):1. |
| [7] | 任鑫;杨怀玉;王福会 等.热腐蚀的盐溶机理研究[J].腐蚀科学与防护技术,2001,13(06):338. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%