炼制了4种不同硅含量(0.04%,0.09%,0.14%和0.36%Si)而其他成分相同的钢,研究了450,480 ℃下其镀层生长及组织变化,探讨了Sebisty现象的形成原因.结果表明,4种含硅钢的镀层生长呈现出典型的Sandelin效应;当锌浴温度从450 ℃升高到480 ℃时,0.04%,0.09%和0.36%Si钢镀层的合金层厚度增加,而0.14%Si钢镀层的合金层厚度减小,呈现出Sebisty现象.利用扫描电镜和电子探针在高倍率下观察了钢基/镀层界面的组织特征后发现,0.14%Si钢镀锌层减薄的原因是Г层由不连续(450 ℃)变为较连续且厚度小于0.5 μm的一层(480 ℃),而连续的Г层的存在会减缓Fe-Zn反应的速度,导致合金层减薄.
参考文献
[1] | Sandlein R W .Galvanizing characteristics of different types of steel[J].Wire and Wire Products,1941,16:28-35. |
[2] | 车淳山,卢锦堂,陈锦虹,许乔瑜,孔纲.热镀锌中圣德林效应微观机理的解释模型[J].材料保护,2004(08):26-28. |
[3] | Schulz W D;Schubert P;Thiele M.An Alternative Approach to Explaining the Effect on the Galvanizing Reaction[A].Amsterdam:EGGA,2003:61-64. |
[4] | Richard F L.Hot-dip galvanizing alloys[J].Journal of The Minerals,Metals & Materials Society,1987(07):39-41. |
[5] | Chen Z W;Kennon N F;See J B et al.Technigalva and other developments in batch hot-dip galvanizing[J].Journal of the Minerals,Metals & Materials Society,1992,44(01):22-26. |
[6] | Marder AR. .The metallurgy of zinc-coated steel [Review][J].Progress in materials science,2000(3):191-271. |
[7] | Kozdras M S;Niessen P .Silicon-Induced Destabilization of Galvanized Coating in the Sandelin Peak Region[J].Metallograghy,1989,22:253-267. |
[8] | Mackowiak J;Short N R.Metallurgy of galvanized coatings[J].International Metals Reviews,1979(01):1-19. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%