为了探讨固化工艺及配方对环氧树脂体系微观结构的影响,研究了用4,4′-二氨基二苯砜(DDS)作固化剂的环氧树脂与聚醚砜(PES)共混体系.采用差示扫描量热法(DSC)和扫描电镜(SEM)研究其相分离和微观结构,并通过改变聚醚砜的用量和固化工艺条件对其进行控制.结果表明,在环氧树脂与聚醚砜间形成了半互穿网络,对应于环氧态和聚醚砜态的玻璃化转变温度彼此靠近.通过控制反应进程和聚醚砜用量,可以获得不同的相结构,加入较多的聚醚砜或采用较高的固化温度,有利于提高聚醚砜增韧环氧树脂的冲击性能.
参考文献
| [1] | 金林生.综述环氧树脂的强韧化[J].热固性树脂,1995(02):52. |
| [2] | 黄锐,王勇,林旭.特种工程塑料聚醚砜[J].塑料科技,1994(01):52-55. |
| [3] | Keizo Y;Takashi I .Structure Development in Epoxy Resin Modified with Poly (ether sulphone)[J].Polymer,1989,30(04):662-667. |
| [4] | Mimura K. .Improvement of thermal and mechanical properties by control of morphologies in PES-modified epoxy resins[J].Polymer: The International Journal for the Science and Technology of Polymers,2000(12):4451-4459. |
| [5] | Kim BS.;Inoue T.;Chiba T. .MORPHOLOGY DEVELOPMENT VIA REACTION-INDUCED PHASE SEPARATION IN EPOXY POLY(ETHER SULFONE) BLENDS - MORPHOLOGY CONTROL USING POLY(ETHER SULFONE) WITH FUNCTIONAL END-GROUPS[J].Polymer: The International Journal for the Science and Technology of Polymers,1995(1):43-47. |
| [6] | 王惠民,梁伟荣.聚醚砜/环氧树脂复合体系的研究[J].高分子材料科学与工程,1999(06):155-157. |
| [7] | 徐修成;殷立新;宋文辉.环氧-聚醚砜体系及其增韧机理的研究[J].宇航材料工艺,1996(01):32-36. |
| [8] | 王汝敏,杨利,郑水蓉,陈立新,蓝立文.聚醚砜增韧双马来酰亚胺树脂研究[J].西北工业大学学报,2002(01):145-150. |
| [9] | [J].粘接,2005,26(02):32. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%