在涂层阳极中掺入稀土Ce对电催化性能的影响报道较少.利用热分解方法在不同温度下制备了不同摩尔分数Ce的三元涂层Ru0.3Ti(0.7～x)CexO2,通过极化曲线测试、交流阻抗谱测试、扫描电镜观察,研究了所制备涂层的电催化活性.结果表明:Ce的掺入量有一个最佳范围,摩尔分数为0.2～0.3时涂层阳极电催化性能最好;适当的热分解温度有利于含Ce涂层阳极性能的提高,最佳温度为450℃;在阳极涂层中引入Ce可以提高其电催化活性.
参考文献
| [1] | Trasatti S .Electrocatalysis:understanding the success of DSA[J].Electrochimica Acta,2000,45:2377. |
| [2] | Beer H B .[P].S Afr Pat 6800834,1968. |
| [3] | Morimitsu M.;Matsunaga M.;Otogawa R.;Tamura H. .Polarization behaviour and lifetime of IrO2-Ta2O5-SnO2/Ti anodes in p-phenolsulfonic acid solutions for tin plating[J].Journal of Applied Electrochemistry,2000(4):511-514. |
| [4] | Fujimura K;Izumiya K;Kawaashima A .Anodically Deposited Manganese- Molybdenum Oxide Anode with High Selectivity for Evolving Oxygen in Electrolysis of Seawater[J].Journal of Applied Electrochemistry,1999,29:765. |
| [5] | Yang CH.;Wen TC.;Lee CC. .Hypochlorite generation on Ru-Pt binary oxide for treatment of dye wastewater[J].Journal of Applied Electrochemistry,2000(9):1043-1051. |
| [6] | Trasatti S;Lodi G.Electrodes of Conductive Metallic Oxides,Part B[M].Amsterdam:Elsevier,1981:521. |
| [7] | Watson P R;Wabner D W .The formation of oxygencontaining organic molecules by the hydrogenation of carbon monoxide using a lanthanum rhodate catalyst[J].Journal of Catalysis,1982,74:282. |
| [8] | Brittain H G.The effect of drying temperature on the temperature- programmed reduction profile of a platinum/rhenium/alumina catalyst[J].Journal of Catalysis,1983(80):334. |
| [9] | 胡吉明,孟惠民,曹楚南,张鉴清,吴继勋,杨德钧.Ti基IrO2+Ta2O5涂层阳极的析氧电催化活性[J].金属学报,2001(06):628-632. |
| [10] | Lassali T A F;Boodts J F C;Bulhoes L O S .Charging processes and electrocatalytic properties of IrO2/TiO2/SnO2 oxide films investigated by in situ A C impedance measurements[J].Electrochimica Acta,1999,44:4203. |
| [11] | Deng T S;Bing J H .Morphology and Electrochemical Activity of Ru-Ti-Sn Ternary-Oxide Electrodes in 1 M NaCl Solution[J].Electrochimica Acta,1993,38(15):2329. |
| [12] | Silva L A D;Alves V A;Silva M A et al.Oxygen Evolution in Acid Solution on IrO2 + TiO2 Ceramic Films.A Study by Impedance,Voltammetry and SEM[J].Electrochimica Acta,1997,42(02):271. |
| [13] | Mahe E;Devillicrs D;Groult H.Electrochemical behaviour of platinum-coated Ta/Ta2O5 electrodes[J].Electrochimica Acta,1999(44):2307. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%