为了在亚磷酸-镍盐体系中获得工艺稳定、耐蚀性好、硬度高的非晶态Ni-P镀层,进行了7因素(温度、电流密度、pH值、硫酸镍浓度、氯化镍浓度、亚磷酸浓度、磷酸浓度)3水平正交试验.优选出制备最佳耐蚀性镀层的工艺条件为:10g/L亚磷酸,180g/L硫酸镍,50g/L氯化镍,45mL/L磷酸,pH值1.8,温度65℃,电流密度6 A/dm2;获得最佳镀层硬度的工艺条件为:40g/L氯化镍,10g/L亚磷酸,180g/L硫酸镍,45 mL/L磷酸,pH值2.2,温度65℃,电流密度6 A/dm2.分析了各因素对镀层耐蚀性和硬度的影响,结果表明,pH值和温度对镀层耐蚀性影响较大,而氯化镍和亚磷酸浓度对镀层硬度影响较大.
参考文献
| [1] | Hu CC.;Bai A. .Composition control of electroplated nickel-phosphorus deposits[J].Surface & Coatings Technology,2001(2/3):181-187. |
| [2] | Yue Zeng;Shaomin Zhou .In situ surface Raman study of the phosphorus incorporation mechanism during electrodeposition of Ni-P alloys[J].Journal of Electroanalytical Chemistry: An International Journal Devoted to All Aspects of Electrode Kinetics, Interfacial Structure, Properties of Electrolytes, Colloid and Biological Electrochemistry,1999(1):79-83. |
| [3] | Fang J;Ye X R .Factors influencing solderability of electroless Ni-P deposits[J].Plating and Surface Finishing,1992,7:44-47. |
| [4] | Morikawa T;Nakade T;Yokoi M et al.Electrodeposition of Ni-P alloys from Ni-citrate bath[J].Electrochimica Acta,1997,42(01):115-118. |
| [5] | 吴玉程,邓宗钢.非晶态镍磷合金的组织结构与性能[J].中国有色金属学报,1998(03):415-419. |
| [6] | 卢燕平.电沉积非晶Ni-P合金的层状结构[J].材料保护,1994(05):5. |
| [7] | 卢燕平.镍-磷合金镀层在盐酸溶液中的耐蚀性[J].材料保护,1991(01):17. |
| [8] | Bai A.;Chuang PY.;Hu CC. .The corrosion behavior of Ni-P deposits with high phosphorous contents in brine media[J].Materials Chemistry and Physics,2003(1):93-100. |
| [9] | 上海科学技术交流站组.正交试验设计法-多因素的试验方法[M].上海:上海人民出版社,1975 |
| [10] | 北京大学力学系概率统计组.正交设计法[M].北京:国防工业出版社,1976 |
| [11] | Crousier J;Hanane Z;Crousier J P .A cyclic volatammetry study of the Ni-P electrodesition[J].Electrochimica Acta,1993,38(2-3):261-266. |
| [12] | 李荻.非晶态镍磷合金电沉积的研究[J].北京航空航天大学学报,1990(04):27. |
| [13] | 陈亚;李士嘉;王春林.现代实用电镀技术[M].北京:国防工业出版社,2003:167. |
| [14] | 于维平;李荻.非晶态电镀方法及应用[M].北京:北京航空航天大学出版社,1992 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%