以Fe-Cr-C合金粉末为原料,采用等离子熔覆技术,在调质C级钢表面制得以原位生成初生相Cr7C3为增强相的新型陶瓷复合材料涂层.利用光子显微镜(OM),扫描电镜(SEM),X射线衍射(XRD)和能量色散谱(EDS)等分析了涂层的显微组织,并在室温干滑动磨损及二体磨料磨损条件下测试了该涂层的耐磨性能.结果表明,涂层组织包括Cr7C3增强相和γ-Fe固溶体与少量Cr7C3构成的共晶;由于Cr7C3/γ-Fe快速凝固复合材料涂层组织细小、均匀,在滑动磨损过程中不易与对偶件黏着、在磨料磨损过程中具有很高的抗切削抗剥落能力,因而在干滑动磨损及二体磨料磨损条件下涂层均具有优良的耐磨性能.
参考文献
| [1] | Aoh J N;Jeng Y R;Chu E L.On the wear behavior of surface clad layers under high temperature[J].WEAR,1999:225-229. |
| [2] | Kim H;Kim Y J.Microstructural evaluations of the plasma transferred arc coated layers on the hardness wear resistance and corrosion for the hardfacing of Niand Co-based alloys[A].,1998:217. |
| [3] | Kim H J;Yoon B H;Lee C H .Wear performance of the Fe-based alloy coatings produced by plasma transferred arc weld-surfacing process[J].Wear,2002,249:846-852. |
| [4] | R. Iakovou;L. Bourithis;G. Papadimitriou .Synthesis of boride coatings on steel using plasma transferred arc (PTA) process and its wear performance[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2002(11/12):1007-1015. |
| [5] | Frangini S.;Masci A.;Di Bartolomeo A. .Cr7C3-based cermet coating deposited on stainless steel by electrospark process: structural characteristics and corrosion behavior[J].Surface & Coatings Technology,2002(2/3):279-286. |
| [6] | Wu X D;Wang D P;Yang S R et al.Tribochemical investigation of tungsten carbidertitanium alloy tribocouples under aqueous lubrication[J].Wear,2000,237:28-32. |
| [7] | Storms E K.The refractory carbides[M].New York:Academic Press,Inc,1967 |
| [8] | Toth L E.Transition metal carbides and nitrides[M].New York:Academic Press,Inc,1971 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%