基于自制的丙烯酸丁酯/苯乙烯/丙烯腈(BA/St/AN)共聚乳液,制备了一种性能优异的水性防锈涂料,研究了防锈颜料和润湿分散剂的种类、用量对涂料及其漆膜性能的影响.当颜基比为0.8,防锈颜料用量为填料总量的50%时,水性防锈涂料耐盐水时间最长.当铵盐分散剂与聚丙烯酸钠以1∶4变化时,水性涂料有最好的综合性能.
参考文献
| [1] | 周海晖,许岩,罗胜联,曾凌三.我国防腐蚀涂料的现状及其发展[J].表面技术,2002(01):5-8. |
| [2] | 沈钟吕.防腐涂料生产与应用技术[M].北京:中国建材工业出版社,1994:1-2. |
| [3] | Sharmin E;Imo L;Ashraf SM;Ahmad S .Acrylic-melamine modified DGEBA-epoxy coatings and their anticorrosive behavior[J].Progress in Organic Coatings: An International Review Journal,2004(1):47-54. |
| [4] | Amo B D;Romagnoli R;Deya C et al.High Performance Water-Based Paints with Non-Toxic Anticorrosive Pigments[J].Progress in organic Coatings,2002,45(01):389-397. |
| [5] | Pokhmurs'kyi V I;Zin' I M;Lyon S B .Inhibition of Corrosion by a Mixture of Nonchromate Pigments in Organic Coatings on Galvanized Steel[J].Materials Science,2004,40(03):383-390. |
| [6] | 张丽,牛明军,刘雪莹,刘大壮,庞勇.水性防锈涂料的配方筛选及防锈性能研究[J].高分子材料科学与工程,2005(01):260-263. |
| [7] | 周立新,程江,杨卓如,张凡.几种水性防锈漆的性能比较[J].合成材料老化与应用,2004(02):23-25. |
| [8] | 何新快,陈白珍,陈洪,周宁波.水性防腐蚀涂料的研制[J].材料保护,2005(01):51-53,69. |
| [9] | 郭清泉,林淑英,陈焕钦.水性金属防腐蚀涂料所用基料现状及发展[J].现代化工,2003(10):25-27,32. |
| [10] | 危恒毅,岳庆磊,宋晓锐,杨辉荣.水性防腐涂料体系[J].精细石油化工进展,2002(04):44-46. |
| [11] | 赵金榜.对环境友好的防锈颜料及作用机理[J].现代涂料与涂装,2002(01):37-39,46. |
| [12] | 谭竹洲.涂料工艺[M].北京:化学工业出版社,2001:11-59. |
| [13] | 骆明.三聚磷酸铝防锈颜料及其改性合成方法[J].化工技术与开发,2004(05):31-33. |
| [14] | 张丽,霍东霞,刘大壮,陈金周.三聚磷酸铝在水性乳胶涂层中的防锈机理研究[J].腐蚀科学与防护技术,2004(05):328-330. |
| [15] | 李家权.复合铁钛粉及其系列防锈漆[J].涂料工业,2003(07):51-53. |
| [16] | 张天胜.表面活性剂应用技术[M].北京:化学工业出版社,2001:17-18. |
| [17] | 张熙,胡爱琼.水性铁红带锈防锈漆[J].上海涂料,2005(01):34-36. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%