分别在磷酸盐和硅酸盐两种体系中研究了不同稀土元素对镁合金微弧氧化的影响.结果表明,提高钕盐浓度可以改善氧化膜的外观、厚度和耐蚀性能.镁合金浸泡在稀土盐溶液中表面能形成稀土转化膜.用稀土转化膜取代镁合金表面的自然氧化膜进行微孤氧化处理,获得的陶瓷层分布更加均匀,表面更为光滑致密.用5%NaCl溶液浸泡48 h的对比腐蚀试验表明,用稀土盐溶液浸泡预处理过的试样耐蚀性显著加强.
参考文献
| [1] | Gerald C.由欧洲和北美两大汽车组织发起的镁研究[J].铸造世界报,2001(01):16-17. |
| [2] | Katya B;Manuele D;Irene C et al.Effect of HCl pretreatment on corrosion resistance of cerium-based conversion coatings on magnesium and magnesium alloys[J].Corrosion Science,2005,47:989-1000. |
| [3] | Anicai L;Masi R;Santamaria M et al.A photoelectrochemical investigation of conversion coatings on Mg substrates[J].Corrosion Science,2005,47(12):2883-2990. |
| [4] | Linstrm R;Johansson L G;Thompson G E et al.Corrosion of magnesium in humid air[J].Corrosion Science,2004,46(05):1141-1158. |
| [5] | Liu ZM;Gao W .Electroless nickel plating on AZ91 Mg alloy substrate[J].Surface & Coatings Technology,2006(16/17):5087-5093. |
| [6] | 边风刚,李国禄,刘金海,刘家浚.镁合金表面处理的发展现状[J].材料保护,2002(03):1-4. |
| [7] | Lianga J;Tiana J;Guoa B G et al.Effects of NaAlO2 on structure and corrosion resistance of micro-are oxidation coatings formed on AM6OB magnesium alloy in phosphateKOH electrolyte[J].Surface and Coatings Technology,2005,199(2-3):121-126. |
| [8] | 魏同波,田军,阎逢元.LY12铝合金微弧氧化陶瓷层的结构和性能[J].材料研究学报,2004(02):161-166. |
| [9] | 陈一胜,张乐观,王勇.稀土对化学镀镍溶液稳定性的影响[J].材料保护,2002(04):38-40. |
| [10] | 郝建民,陈宏,张荣军,蒋百灵.微弧氧化和阳极氧化处理镁合金的耐蚀性对比[J].材料保护,2003(01):20-21. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%