研究了电镀锌板上一种新型ca2+、Zn2+、Mn2+三元磷化工艺.通过扫描电镜(SEM)、光电子能谱(XPS)、电化学交流阻抗等方法研究了Ca2+浓度对磷化膜晶粒形态、膜层结构及膜层耐腐蚀性能的影响.采用时间电位曲线和扫描电镜(SEM)分析研究了这种新型三元磷化膜在镀锌板上的生长机理且与传统zn2+、Mn2+、Ni2+三元磷化膜微观形态及耐蚀性能进行了比较.结果表明,在最佳Ca2+浓度下,电镀锌板上三元磷化膜具有类似钢铁表面粒状磷化膜的微观形态,比传统三元磷化膜晶粒结构更细致、耐蚀性更好.
参考文献
[1] | Hara M.;Ichino R.;Okido M.;Wada N. .Corrosion protection property of colloidal silicate film on galvanized steel[J].Surface & Coatings Technology,2003(0):679-681. |
[2] | Ogle K;Tomandl A;Meddahi N et al.The alkaline stability of phosphate coatings I:ICP atomic emission spectroelectrochemistry[J].Corrosion Science,2004,46:979-995. |
[3] | Akhtar AS;Susac D;Glaze P;Wong KC;Wong PC;Mitchell KAR .The effect of Ni2+ on zinc phosphating of 2024-T3 Al alloy[J].Surface & Coatings Technology,2004(2/3):208-215. |
[4] | D. Zimmermann;A.G. Munoz;J.W. Schultze .Microscopic local elements in the phosphating process[J].Electrochimica Acta,2003(20/22):3267-3277. |
[5] | Amatch A;Pahlevani B .Effect of rare earth metal addition on the surface morphology and corrosion resistance of hotdipped zinc coating[J].Corrosion Science,2002,44:2321-2331. |
[6] | Hara M.;Ichino R.;Okido M.;Wada N. .Corrosion protection property of colloidal silicate film on galvanized steel[J].Surface & Coatings Technology,2003(0):679-681. |
[7] | Arenas M A;Damborenea J J .Surface characterization of cerium layers on galvanized steel[J].Surface and Coatings Technology,2004,187:201-325. |
[8] | Zin I M;Lyon S B;Pokhmurskii V I .Corrosion control of galvanized steel using a phosphate/calcium ion inhibitor mixture[J].Corrosion Science,2003,45:777-788. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%