采用非醇盐溶胶-凝胶工艺可获得Fe与Si摩尔比达4.5/1的均匀凝胶,发现可以通过控制SiO2的含量和热处理条件来控制相结构和晶粒尺寸,热处理过程中α-Fe相是由Fe3O4相还原而来,材料中有大量氧参与反应是工艺中采用了沉淀胶溶步骤的结果,最终制备了纳米复合Fe-SiO2粉体.
参考文献
[1] | Andres R P;Averback R S;Brown W L;Brus L E CroddardⅢ W A Kaldor A Lowe S G Moscovits M Peorey P S Riley S J Scegal R W Spaepen F,Wang Y .[J].Journal of Materials Research,1989,4:704. |
[2] | Chatterjee A;Chakravorty D .[J].Journal of Physics D:Applied Physics,1989,22:1386. |
[3] | Granqvist C G;Buhrman R A .[J].Journal of Applied Physiology,1976,47:2200. |
[4] | Abeles B;Sheng P;Coutts M D;Arie Y .[J].Advances in Physics,1975,24:204. |
[5] | Roy R A;Roy R .[J].Materials Research Bulletin,1984,19:169. |
[6] | Xiao Gong;Chien C L .[J].Applied Physics Letters,1987,51:1280. |
[7] | Wang Jian-ping;Luo He-lie .[J].Journal of Magnetism and Magnetic Materials,1994,131:54. |
[8] | Wang Jian-ping;Han De-hua;Luo He-lie;Gao Nei-Fai,Liu Yuan-Yuan .[J].Journal of Physics D:Applied Physics,1994,27:2002. |
[9] | 理学电机株式会社分析中心;浙江大学分析测试中心.X射线衍射手册[J].理学电机,1987:73. |
[10] | 武汉大学.无机化学下册[M].北京:高等教育出版社,1983:465-466. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%