分析了陶瓷,玻璃等脆性材料的断裂机理和表征.指出了脆性材料的失效过程的三种不同的裂纹发展模式.实验研究了玻璃在静载下的亚临界裂纹扩展特征及其受双向应力的影响.从而为脆性材料的可靠性和寿命评价提供理论基础和手段.
参考文献
[1] | Broek D.Elementary engineering mechanics[M].USA:Kluwer Academic Publisher,1986 |
[2] | Steinbrech R W .R-Curve behaviour of ceramics[J].Fracture Mechnics of Ceramics,1992,9:187. |
[3] | 包亦望,Steinbrech R W.玻璃在平面双向和单向应力状态下慢裂纹扩展特性[J].硅酸盐学报,1998(05):604-609. |
[4] | DillS J;Bennison S J;Dauskardt R H.Subcritical Crack-Growth Behaviour of Borosilicate Glass under Cyclic Loads:Evidence of a Mechanical Fatigue Effect[J].Journal of the American Ceramic Society,1997(03):773-776. |
[5] | Eftis J;Subramonian N;Liebowitz H .Biaxial Load Effects on the Crack Border Elastic Strain Energy and Strain Energy Rate[J].Engineering Fracture Mechanics,1997,9:753-764. |
[6] | Kibler J J;Roberts R .The Effects of Biaxial Stresses on Fatigue and Fracture[J].Journal of Engineering for Industry-Transactions of the ASME,1970,92:727. |
[7] | Mencik J.Strength and Fracture of Glass and Ceramics[M].New York:Elsvier Science Publishing,1992:130. |
[8] | 包亦望;金宗哲.陶瓷材料的疲劳表征[A].武汉,1993:11. |
[9] | Wang E Z;Shrive N G .Brittle Fracture in Compression:Mechanisms[J].Models and Criteria Eng Fract Mechanics,1995,52(06):1107-1126. |
[10] | Bao Yiwang;Steinbrech E W .Strain Criterion of Fracture in Brittle Materials[J].Journal of Materials Science Letters,1997,16(180):153. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%