本文采用常压烧结工艺制备ZrO2增韧莫来石陶瓷(ZTM).通过调整ZrO2、Y2O3含量制得不同组成的ZTM材料,其强度随ZrO2加入量的增加经历了先上升而后下降的过程.在不同组成下,材料的强韧化机理不同.当ZrO2≤30vol%时,ZTM材料是以应力诱导相变增韧为主;ZrO2>30vol%(如ZT M40(2Y)),材料则以微裂纹,裂纹偏转等强韧化机理为主;并且分散相ZrO2晶粒的大小及分布均匀性等对强韧化机理的发挥有很大影响.
参考文献
[1] | Kamiaki Y;Mateuehita S et al.Colloidal processing and mechanical properties of whisker reinforced mullite matrix composites[J].Journal of the American Ceramic Society,1991,74:2438-2442. |
[2] | Ishistuka M;Sato T et al.Sintering and mechanical properties of yttria-doped tetragonal ZrO2 polycrystal/mullite composites[J].Journal of the American Ceramic Society,1987,70:C342-346. |
[3] | Prochazka S;Wallace J et al.Microstructures of sintered mullite-ZrO2 composites[J].Journal of the American Ceramic Society,1983,66:C125. |
[4] | Yuan Q-M;Tan J -Q et al.preparation and properties of ZrO2 toughened mullite ceramics[J].Journal of the American Ceramic Society,1986,69:265. |
[5] | 杜海燕 .Y-TZP陶瓷的结构缺陷控制及其复相改性[D].天津大学,1999. |
[6] | Mori T;Kosugi N et al.Microstructure and mechanical properties of mullite sintered bodies containing Y2O3[J].Journal of the Ceramic Society of Japan,1990,98:1307. |
[7] | Yoan C K;Chen I-w .Superplastic flow of mullite-ZrO2 composites[J].British Ceramic Transactions,1990,6:567-577. |
[8] | 徐跃萍 等.ZrO2-Y2O3超细粉烧结动力学的研究[J].硅酸盐学报,1992,20(01):35. |
[9] | 黄书珍 .ZTM陶瓷工艺参数的优化研究[D].天津大学,1989. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%