本文用二氯氧锆醇溶液与醋酸盐相互作用制得醋酸氧锆的溶胶。将溶胶拉丝，烧结后即可得到ZrO2纤维，通过XRD分析确定ZrO2纤维的物相为亚稳态的四方相。对ZrO2纤维的前驱体ZrO（AC）2进行热重（TG）和差热（DTA）分析，对ZrO2纤维进行扫描电镜（SEM）分析，并对纤维进行抗拉强度测试。在此基础上讨论了ZrO2纤维的烧结过程。
参考文献
| [1] | Yermolenko I N;Vityaz P A;Ulyanova T M.Synthesis and sintering of ZrO2 fibers[J].Sprechsaal,1985(04):118. |
| [2] | Abe Y.;Tomioka H.;Gunji T.;Nagao Y.;Misono T.;Kudo T. .Preparation of continuous zirconia fibres from polyzirconoxane synthesized by the facile one-pot reaction[J].Journal of Materials Science,1998(7):1863-1870. |
| [3] | De G;Chatter A;Ganguli D.Zirconia fibers from the zirconium-propoxide-acetylacetone-water-isopropanol system[J].Journal of Materials Science Letters,1990(09):845-846. |
| [4] | Abe Y;Tomioka H;Gunbi T.A one-pot synthesis of polyzirconoxane as a precursor for continuous zirconia fibers[J].Journal of Materials Science,1994(13):960-962. |
| [5] | 吴建锋,徐晓虹,孙淑珍,任永光.（MgO·Y2O3）稳定ZrO2的研究[J].硅酸盐通报,1999(05):69-71. |
| [6] | 高宣铉;赵孟喜 .四方ZrO2的X-射线衍射鉴定特征及定量分析中的几个问题[J].耐火材料,1994,28(05):273. |
| [7] | 郑绣华;孟昭延;王凤合 .ZrO2陶瓷中Zr4+和Y3+的近邻结构与相稳定性[J].材料研究学报,1999,13(02):172. |
| [8] | 尹邦跃,王零森,樊毅,张金生.乙二醇在络合物溶胶-凝胶法中的应用研究[J].硅酸盐学报,1999(03):337-341. |
| [9] | Morita H;Yamane H .Alunina fibers from poly[J].Journal of Applied Polymer Science,1990,40:753-767. |
| [10] | Maki T;Sakka S .Preparation of alumina fibers by sol-gel method[J].Journal of Non-Crystalline Solids,1988,100:303-308. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%