研究了多种烧结助剂对氮化硅烧结性能和烧结过程的影响.研究表明,多组分助剂比单一组分助剂对氮化硅的助烧效果好,其中稀土氧化物和MgO-Al2O3-SiO2体系比较受重视.
参考文献
| [1] | Mamoru M;Gunter P.Recent progress in silicon nitride and silicon carbide ceramicsc[J].MRS Bulletin,1995(02):19-21. |
| [2] | Hoffmann M J.High-temperature properties of Si3N4 cera-mics[J].MRS Bulletin,1995(02):28-30. |
| [3] | Mamoru N;Naoto H;Hideki H.Microstructural design and control of silicon nitride ceramics[J].MRS Bulletin,1995(02):38-40. |
| [4] | 陈源;黄莉萍;孙兴伟 等.烧结助剂对氮化硅陶瓷高温性能的影响[J].硅酸盐学报,1997,25(02):183-187. |
| [5] | 于之东;刘大成 .氮化硅陶瓷的烧结[J].中国陶瓷,1999,35(03):21-23,25. |
| [6] | Braue W;Wotting G;Ziggler G.Progress in nitrogen cerami-cs.Riley F L,ed[M].New York: Maetinus Niihoff Pub,1983:883-887. |
| [7] | Drew P;Simon J P D;Kartik S.The microstructures of silicon nitride ceramics during hot-pressed transformations[J].Journal of Materials Science,1974(09):261-263. |
| [8] | 沈中毅;孙继荣;刘世超 等.氮化硅(Si3N4)-稀土氧化物陶瓷的超高压烧结研究[J].高压物理学报,1997,25(02):183-187. |
| [9] | 刘得利 .氮化硅陶瓷生产用粉体和烧结助剂[J].陶瓷工程,2000,34(04):29-30. |
| [10] | 徐友仁;黄莉萍;符锡仁.添加稀土氧化物的热压氮化硅陶瓷[J].中国科学A辑,1985(04):384-387. |
| [11] | Bratton R J;Anderson C A;Lange F F.Nitrogen Ceramics[M].Leyden:Noordholf International Publishing,1977:805. |
| [12] | 徐鑫,黄莉萍,符锡仁.β-Si3N4粉末烧结及其显微结构形成[J].无机材料学报,2000(01):50-54. |
| [13] | 徐友仁;沈荣水;马利泰 等.添加稀土氧化物热压氮化硅陶瓷的蠕变机制[J].无机材料学报,1991,6(02):151-159. |
| [14] | 齐震川;刘志厚.烧结Si3N4的力学性能[J].国外耐火材料,1991(05):793-804. |
| [15] | 杨海涛,徐润泽,黄培云.MgO-CeO2烧结助剂对常压烧结氮化硅陶瓷致密化和性能的影响[J].中国有色金属学报,1996(03):91-95. |
| [16] | 杨海涛;徐润泽;黄培云 .Si3N4-MgO-CeO2陶瓷烧结过程中MgO的自动析出[J].中南工业大学学报(自然科学版),1996,27(05):573-577. |
| [17] | 刘宏;王连增;李元宝 等.Si3N4-MgAl2O4-Al2O3系材料无压烧结的研究[J].中国陶瓷,1995,31(04):7-11. |
| [18] | 李文宏;顾培芷;赵惠琴 等.Si3N4-MgO*Al2O3-ZrO2系材料的无压烧结研究[J].硅酸盐学报,1987,6(02):29-32. |
| [19] | 袁力健;严东生;矛志琼 .低温热压氮化硅的烧结机理[J].硅酸盐学报,1989,17(06):530-536. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%