采用湿化学法合成出组成为(Ag0.9Na0.1)(Nb0.6Ta0.4)O3的复合氧化物,应用TG-DTA,XRD,SEM等分析手段对该陶瓷粉体的制备条件进行了研究.实验结果表明:该瓷粉的合成温度为800℃,灼烧时间3h,晶体为六方晶系,平均粒径为34nm.用传统成瓷工艺在1040～1060℃下制得瓷件的介电常数ε >500,损耗角正切tgδ为4.5×10-4.
参考文献
| [1] | Kania A .Flux growth of AgTaxNb1-xO3(ATN) solid solution single crystals[J].Journal of Crystal Growth,1989,96:703-704. |
| [2] | Fortin W.;Grigas J.;Kania A.;Kugel GE. .MANIFESTATION OF NB DYNAMICS IN RAMAN, MICROWAVE, AND INFRARED SPECTRA OF THE AGTAO3-AGNBO3 MIXED SYSTEM[J].Journal of Applied Physics,1996(8 Pt.1):4273-4282. |
| [3] | Kania A. .Dielectric properties of Ag(1-x)A(x)NbO(3) (A : K, Na and Li) and AgNb1-xTaxO3 solid solutions in the vicinity of diffuse phase transitions[J].Journal of Physics, D. Applied Physics: A Europhysics Journal,2001(10):1447-1455. |
| [4] | 陈长庆,吴霞宛,袁廷志,朱征,林曼红.（Ag1-xNax）（Nb1-yTay）O3陶瓷介电性能的研究[J].硅酸盐学报,2003(03):308-311. |
| [5] | Johnson D W .Powder preparation nonconventional[J].American Ceramic Society Bulletin,1981,60(02):221-224. |
| [6] | 武汉大学化学系.稀土元素分析化学(上)[M].北京:科学出版社,1981:69. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%