Mg4Nb2O9具有与α-Al2O3相同的刚玉型晶体结构,可望成为取代氧化铝陶瓷的新一代高Q值基板材料.TG-DTA(热失重-差热)和X射线衍射分析表明,Mg4Nb2O9的合成温度低于900℃.在900～1400℃温度范围内,采用固相反应法合成了Mg4Nb2O9化合物.相结构检测分析表明,生成物中除了主晶相Mg4Nb2O9外,还含有MgNb2O6和MgO2种物相;Mg4Nb2O9相的最佳合成温度为1300℃.同时,对Mg4Nb2O9陶瓷的微波性能进行了测试分析,得到了ε为13.1,Q·f为136682 GHz的较好性能.
参考文献
| [1] | Lee H J;Kaf I T;Hong K S .Dielectric properties of AB2O6compounds at microwave frequencies(A = Ca, Mg, Mn, Co, Ni,Zn, and B=Nb, Ta)[J].Japanese Journal of Applied Physics,1997,36:L1318-L1320. |
| [2] | Sohn J H;Inaguma Y;Yoon S O et al.Kim microwave dielectric characteristics of ilmenite-type titanates with high Q values[J].Japanese Journal of Applied Physics,1994,33(9B):5466-5470. |
| [3] | 曲远方.功能陶瓷及应用[M].北京:化学工业出版社,2003:138-144. |
| [4] | Kumada N;Taki K;Kinomura N .Single crystal structure refinement of a magnesium niobium oxide: Mg4Nb2O9[J].Materials Research Bulletin,2000,35(07):1017-1021. |
| [5] | Ogawa H;Kan S;Ishihara S .Yutaka higashida crystal structure of corundum type Mg4(Nb2-xTax) O9 microwave dielectric ceramics with low dielectric loss[J].Journal of the European Ceramic Society,2003,23(14):2485-2488. |
| [6] | You Y C;Park N;Jung K H et al.Luminescence of cerium doped Mg4Nb2O9 phosphor[J].Journal of Materials Science Letters,1994,13:1682-1683. |
| [7] | You Y C;Park H L;SongY G et al.Stable phases in the MgO-Nb2O5 system at 1250℃[J].Journal of Materials Science Letters,1994,13:1487-1489. |
| [8] | Joy P A .Low temperature synthesis of Mg4Nb2O9[J].Materials Letters,1997,32(5-6):347-349. |
| [9] | Bruck E;Rout R K;Raymakers R J et al.Crystal growth of compounds in MgO-Nb2O5 binary system[J].Journal of Crystal Growth,1993,128:842-845. |
| [10] | Huang C L;Weng M H .Low - fire dielectric ceramics for microwave applications[J].Materials Letters,2000,43(1-2):32-35. |
| [11] | Screedhar K;Pavaskar N R .Synthesis of MgTiO3 and Mg4Nb2O9using stoichiometrically excess MgO[J].Materials Letters,2002,53(06):452-455. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%