通过直接浸渗法制备了致密的MoSi2/SiC复合材料,在室温下该材料的强度为(248±25)MPa,1600℃下该材料的强度为(205±20)MPa,室温下显微硬度为12.6 GPa,断裂韧性为3.6 MPa·m1/2.同时分析了Si分压对材料表面形貌的影响.
参考文献
| [1] | Sremitzke M .Review structural ceramic nanocomposites[J].Journal of the European Ceramic Society,1997,17(09):91061-82. |
| [2] | Dressier M;Riedel R .Process in silicon-based non-oxide structural ceramics[J].International Journal of Refractory Metals and Hard Materials,1997,15:13-47. |
| [3] | Nihara K;Hario T.The Orreation Between Interiace Structure and Mechanical Propertis for Silicon Nitride Based Nanocomposites Grain Boundary Controlled Propertis of Fine Ceramics[M].London:Elsever,1992:103-111. |
| [4] | Hirano T;Nihara K .Microstrcture and mechanical properties of Si3N4/SiC composite[J].Materials Letters,1995,22:249-254. |
| [5] | Iturriza I;Castro F .Sinter and siter-HIP of silicon nitride ceramics with yttri and alumina additions[J].Journal of Materials Science,1989,24(06):2047-2056. |
| [6] | Sasaki G;Nakase H .Mechanical properties and microsturcture of Si3N4 matrix composite with nano-metre scale SiC particle[J].Journal of the Ceramic Society,1992,100(04):536-409. |
| [7] | Ohji T.;Choa YH.;Niihara K.;Jeong YK. .Strengthening and toughening mechanisms of ceramic nanocomposites[J].Journal of the American Ceramic Society,1998(6):1453-1460. |
| [8] | Lim G B;Yano T;Iski T .Microstructure and mechanical properties of RB-SiC/MoSi2 composite[J].Journal of Materials Science,1989,24(04):4144-4151. |
| [9] | 甘国友,孙加林,陈敬超,陈永翀,严继康.Mo-Si-C三元系组元化学势稳定性相图[J].硅酸盐学报,2002(02):193-197. |
| [10] | 张强.钼合金[M].北京:冶金工业出版社,1983 |
| [11] | 刘伯威,潘进,樊毅,张金生.（SiCp+C）/MOSi2复合材料的组织结构及力学性能[J].中国有色金属学报,2001(04):631-637. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%