氧化锆是一种具有特殊作用的氧化物并受到越来越多的关注.作者利用阳离子表面活性剂(CTAB)的辅助途径,通过前期的制备工艺成功实现了金属铝对纳米氧化锆的掺杂改性.借助XRD,TEM,EDS,Uv-vis以及N2吸附-脱附等方法对样品进行了表征分析;研究表明:金属铝离子能成功地进入氧化锆当中,掺杂改性后的氧化锆相对未掺杂的氧化锆有明显的蓝移,热稳定性显著提高,并且有一定的微孔结构.
参考文献
| [1] | 张立德.纳米材料研究的新进展及在21世纪的战略地位[J].中国粉体技术,2000(01):1-5. |
| [2] | Tanabe K;Yamaguchi T .Acid-base bifunctional catalysis by ZrO2 and its mixed oxides[J].Catalysis Today,1994,20:185-197. |
| [3] | Bokhim X;Morales A;Garcia-Ruiz A et al.Transformation of yittrium-doped hydrated zirconium into tetragonal and cubic nanocrystalline zirconia[J].Journal of S State Chem,1999,142:409-418. |
| [4] | Huang Yinyan;Zhao Biying;Xie Youchang .Prearation of zirconia-based acid catalysts from zirconia zerogel of tetragonal phase[J].Applied Catalysis,1998,172:327-331. |
| [5] | Mekhemer GAH.;Ismail HM. .Structure analysis of phosphated zirconia catalysts using XRD and nitrogen adsorption methods[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2000(2/3):227-235. |
| [6] | 陈航榕,施剑林,杨勇,李蕾,阮美玲,严东生.钇掺杂介孔氧化锆材料的合成与表征[J].化学学报,2003(09):1441-1443. |
| [7] | Sominski E;Gedanken A;Perkas N et al.The sonochemical preparation of a mesporous NiO/yttria stabilized zirconia composite[J].Microporous and Mesoporous Materials,2003,60:91-97. |
| [8] | Mamak M.;Ozin G.;Coombs N. .Mesoporousyttria-zirconia and metal-yttria-zirconia solid solutions for fuel cells[J].Advanced Materials,2000(3):198-202. |
| [9] | Mamak M;Coombs N;Ozin G .Self-assembling solid oxide fuel cell materials:mesporous yttria-zirconia and metal-yttria-zirconias solid solutions[J].Journal of the American Chemical Society,2000,122:8923-8939. |
| [10] | 温立哲,余忠民,黄慧民,周立清,邓淑华.纳米氧化锆的制备及其干燥技术[J].广东工业大学学报,2002(01):63-69,105. |
| [11] | E. Zhao;S. E. Hardcastle;G. Pacheco;A. Garcia;A. L. Blumenfeld;J. J. Fripiat .Aluminum-doped mesoporous zirconia obtained from anionic surfactants[J].Microporous and Mesoporous Materials,1999(1/2):9-21. |
| [12] | Chen Hangrong;Shi Jianlin;Yu Jian et al.One-step synthesis of hydrothermally stable cubic mesoporous aluminosilicates with a novel partical structure[J].Microporous and Mesoporous Materials,2000,39(1-2):171-176. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%