本文以正硅酸乙酯(TEOS)为原料,以多羟基倍半硅氧烷(polyhedral oligomeric silsesquioxanes)为疏水改性试剂,通过二氧化碳超临界干燥制备了表观密度为30～150mg/cm3、可加工的疏水SiO2气凝胶.采用傅立叶变换红外(FTIR)对疏水型SiO2气凝胶的结构和性能进行了研究.
参考文献
| [1] | Schwertfeger F.;Schmidt M.;Frank D. .Hydrophobic waterglass based aerogels without solvent exchange or supercritical drying[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,1998(1):24-29. |
| [2] | Tamon H.;Okazaki M.;Kitamura T. .Preparation of silica aerogel from TEOS[J].Journal of Colloid and Interface Science,1998(2):353-359. |
| [3] | 李伟,王霞瑜,张平,黄舸,贺小华.溶胶-凝胶法制备疏水型SiO-2气凝胶[J].材料科学与工程,2002(01):58-60. |
| [4] | 莫红军;王宁飞;樊学忠.密度SiO2气凝胶的制备及性质表征[J].化学世界,1999(01):12-16. |
| [5] | Yokogawa H;Yokoyama M.Hydrophobic silica aerogels[J].Journal of Non-Crystalline Solids,1995(186):23-29. |
| [6] | 任洪波,张林,邓龙江.杂化溶胶改性紫外光固化胶粘剂的研究[J].强激光与粒子束,2004(08):1013-1016. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%