以TiO2和ZrO2作为晶核剂,采用"两步法"热处理工艺,制备了透明、零膨胀的Li2O-Al2O3-SiO2(LAS)系微晶玻璃.利用X射线衍射分析和扫描电子显微镜对该微晶玻璃的物相和微观结构进行分析,结果表明:微晶玻璃中析出大量β-锂辉石晶粒,其晶粒半径仅为50～100nm.LAS系微晶玻璃热膨胀系数在20～400℃范围内趋向于零,而在400～750℃范围内热膨胀系数不断升高,趋向于8×10-7/K.该LAS系微晶玻璃具有良好的透光性能,于可见光范围内透过率为70%.
参考文献
| [1] | Wolfram H;George B.Glass-Ceramic Technology[M].Westerville:The American Ceramic Society,2002 |
| [2] | 楼贤春,程金树,郑伟宏,刘清.锂铝硅系统微晶玻璃热处理制度优化研究[J].玻璃,2005(03):7-10,26. |
| [3] | Tauch D;Russel C .Glass-ceramics with zero thermal expansion in the system BaO/Al2O3/B2O3[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2005(27/29):2294-2298. |
| [4] | Tauch D;Russel C .Thermal expansion of glass-ceramics in the system BaO/Al2O3/B2O3[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2005(43/45):3483-3489. |
| [5] | 李天伶.β-锂辉石的晶体化学性质及其低热膨胀性的结构解释[J].硅酸盐通报,1995(02):27-32. |
| [6] | 刘树江,卢安贤.热处理制度对Li2O-Al2O3-SiO2系统玻璃析晶及热膨胀系数的影响[J].中南工业大学学报(自然科学版),2002(05):513-516. |
| [7] | 康利军,刘彤,苏志梅,李同海,孔玉娥,王丽莉,赵京.β-锂霞石负膨胀微晶玻璃的制备技术及结构特征[J].功能材料,2005(06):825-827. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%