采用EDTA-柠檬酸盐法合成Bi2V0.9Co0.1O5.5-δ超细粉体,采用TG-DSC、XRD、SEM等测试方法对粉体的合成过程、晶体结构和颗粒形态进行了表征.研究结果表明,经450℃热处理可以得到具有单一Aurivillus结构的超细粉体(约为200nm).在620℃下烧结3h可制备出致密的陶瓷样品,陶瓷样品的平均晶粒粒径约为3μm,相对密度达到94.5%.采用交流阻抗谱法研究了Bi2V0.9Co0.1O5.5-δ陶瓷的氧离子导电性能,发现在600℃时Bi2V0.9Co0.1O5.5-δ陶瓷的氧离子电导率达1.0×10-1S·cm-1.
参考文献
[1] | Achary S N;Mathews M D;Patwe S J et al.High-temperature X-ray diffraction and dilatometric studies on some oxygen ion conducting compounds[J].Journal of Materials Science Letters,1999,18:355-357. |
[2] | Chadwick A V;Maltese C colli C;Morrison G et al.EXFS studies of the cation site in BIMEVOX fast-ion conductors[J].Solid State Ionics,1999,119:79-84. |
[3] | Yaremchenko AA.;Naumovich EN.;Samokhval VV.;Kharton VV. .Oxygen ionic and electronic conductivity of La-doped BIMEVOX[J].Solid state ionics,1998(3/4):227-236. |
[4] | I. Abrahams;F. Krok;J.A.G. Nelstrop .Defect structure of quenched γ-BICOVOX by combined X-ray and neutron powder diffraction[J].Solid state ionics,1996(1/4):57-65. |
[5] | S. Lazure;Ch. Vernochet;R.N. Vannier;G. Nowogrocki;G. Mairesse .Composition dependence of oxide anion conduction in the BIMEVOX family[J].Solid state ionics,1996(1/4):117-123. |
[6] | Jacobsoone V.;Boivin JC.;Follet-Houttemane C. .Evidence of a new bismuth vanadium zinc oxyfluoride with the BIMEVOX structure[J].Solid state ionics,1998(Special Issue SI):607-613. |
[7] | P. Kurek;M.W. Breiter .Thermal stability and ionic conductivity of the BIMEVOX.10 ceramics (ME = Zn, Ni)[J].Solid state ionics,1996(1):131-135. |
[8] | F. Krok;I. Abrahams;D.G. Bangobango;W. Bogusz;J.A.G. Nelstrop .Electrical and structural study of BICOVOX[J].Solid state ionics,1996(1):261-266. |
[9] | Abrahams I;Krok F;Nelstrop J A G .Defect Structure of quenched γ-BICOVOX by combined X-ray and neutron powder diffraction[J].Solid State Ionics,1996,90:57. |
[10] | Cho H;Sakai G;Shimanoe K et al.Behavior of oxygen concentration cells using BiCuVOx oxide-ion conductor[J].Sensors and Actuators B:Chemical,2005,108:335-340. |
[11] | A.Kezionis;W.Bogusz;F.Krok .Relaxation dispersion of ionic conductivity of BICOVOX[J].Solid state ionics,1999(1/4):145-150. |
[12] | M.C.Steil and P.Labrune .BICOVOX: sintering and grain size dependence of the electrical properties[J].Journal of the European Ceramic Society,1999(6/7):815-818. |
[13] | M.J. Godinho;P.R. Bueno;M.O. Orlandi .Ionic conductivity of Bi_4Ti_(0.2)V_(1.8)O_(10.7) polycrystalline ceramics obtained by the polymeric precursor route[J].Materials Letters,2003(16/17):2540-2544. |
[14] | Andre Cornelis van Veen;David Farrusseng;Claude Mirodatos .Novel preparation of BIMEVOX materials assisting in elementary step resolved investigations of the oxygen transfer at the surface[J].Desalination: The International Journal on the Science and Technology of Desalting and Water Purification,2002(1/3):41-47. |
[15] | Jennifer W P;Jackie Y Y;Hans C Z L .Sol-gel synthesis of α-Bi2VO5.5 using a soluble bismuth precursor[J].Materials Letters,1995,25:157-160. |
[16] | Hervoches CH;Steil MC;Muccillo R .Synthesis by the polymeric precursor technique of Bi2Co0.1V0.9O5.35 and electrical properties dependence on the crystallite size[J].Solid state sciences,2004(2):173-177. |
[17] | M.H. Paydar;A.M. Hadian;G. Fafilek .Studies on preparation, characterisation and ion conductivity of TI-CU double substituted Bi_4V_2O_(11)[J].Journal of the European Ceramic Society,2001(10/11):1821-1824. |
[18] | O. Thery;R.N. Vannier;C. Dion;F. Abraham .Preparation, characterization and oxide ion conductivity in U-substituted Bi_4V_2O_(11)[J].Solid state ionics,1996(1/4):105-110. |
[19] | C.K. Lee;A.R. West .Thermal behaviour and polymorphism of BIMEVOX oxide ion conductors including the new materials: Bi_4V_2O_(11): M; M = La, Y, Mg, B[J].Solid state ionics,1996(1):235-239. |
[20] | Lee C.K.;Ong C.S. .Synthesis and characterization of rare earth substituted bismuth vanadate solid electrolytes[J].Solid state ionics,1999(3/4):301-310. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%