分别采用普通干压法和粉末电磁压制法成型,制备xPMnS-(1-x)PZN压电陶瓷,探讨了成型工艺对材料结构与性能的影响.结果表明:粉末电磁压制法成型的样品致密度均达到了95%以上,压电与介电性能均高于干压法制备的材料,当x=0.55时综合性能可达到最佳,分别为:kp=0.46,Qm=391,tanδ=0.54%,εT33/ε0 =1739,d33=347pC/N.
参考文献
[1] | Managels J A;Messing G L.Advances in Ceramics Vol.9:Forming of Ceramics[J].American Ceramic Society of Bulletin,1984:241-245. |
[2] | Onoda Jr G Y;Hench L L.Ceramics Processing Before Firing[M].New York:Wiley-Intersciences,1978:235-251. |
[3] | Clyens S;Johnson W;S T S .Al-Hassni[P].UK 577875,1976. |
[4] | Tamari N;Kondoh I;Tanaka T et al.Effect of spark plasma sintering on densification.Mechanical properties and cutting performance of titanium carbide whisker/alumina composite ceramics[J].Journal of the Ceramic Society of Japan,1997,105(10):911-915. |
[5] | 黄尚宇,常志华,王立峰,吴莉花,张猛,姜奎华,王仲仁.板坯电磁成形载荷计算方法及分布特性[J].中国有色金属学报,1998(03):441-446. |
[6] | ZHOU Jing,CHEN Wen,Sun Huajun,XU Qing,ZHENG Jinxia.Effects of Sintering Technology on PMZN Piezoceramics Properties[J].武汉理工大学学报(材料科学版)英,2002(01):27-29. |
[7] | PSN-PZN-PMS-PZT五元系压电陶瓷性能的研究[J].压电与声光,2005(05):510-513. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%