在蒸气养护工艺中,水化热与蒸养温度(恒温温度60 ℃)的协同下混凝土内部温度易超过80 ℃,使水化初期生成的钙矾石分解,并在温度降低以后,在硬化混凝土内重新生成.合理控制[SO42-]/[AlO2-]的阀值提高钙矾石分解温度,增强其稳定性;掺加矿渣等矿物掺和料可以降低混凝土中心水化热,从而避免达到钙矾石的分解温度,同时降低孔隙液的pH值,生成非膨胀性钙矾石.
参考文献
| [1] | Lawrence C D .Mortar expansions due to delayed ettringite formation effects of curing period and temperature[J].Cement and Concrete Research,1995,25(04):903-914. |
| [2] | 朱伯芳.大体积混凝土温度应力与温度控制[M].北京:中国电力出版社,1999 |
| [3] | Yang R;Lawrence C D;Sharp H J .Delayed ettringite formation in 4-year old cement pastes[J].Cement and Concrete Research,1996,26(10):1649-1659. |
| [4] | Diamond S .Delayed ettringite formation-p rocess and problems[J].Cement Concrete Compositie,1996,18(02):205-215. |
| [5] | 阎培渝,覃肖,杨文言.大体积补偿收缩混凝土中钙矾石的分解与二次生成[J].硅酸盐学报,2000(04):319-324. |
| [6] | Stark J;Bollmann K .Delayed Ettringite Formation in Concrete[OL].http://www.google.com |
| [7] | 陈胡星,叶青,沈锦林,胡国君,楼宗汉.钙矾石的长期稳定性[J].材料科学与工程,2001(02):69-71. |
| [8] | Mehta P K.Mechanism of sulfate attack on portland cement concrete-another look[J].Cement and Concrete Research,1983(13):401-406. |
| [9] | 游宝坤,李光明,韩立林.大体积补偿收缩混凝土的结构稳定性问题[J].混凝土,2001(05):7-11. |
| [10] | 姜奉华,徐德龙.Q相-C2S-C4AF-C12A7水泥作为膨胀剂的研究[J].硅酸盐通报,2005(04):107-109,113. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%