研究了ZrB2-SiC复合材料的凝胶注模成型技术.着重讨论了分散剂、pH值、固相体积含量、有机单体等对ZrB2-SiC复合材料料浆的影响;分析了凝胶注模成型后,排胶前复合材料素坯断面的显微结构以及相对应的烧结体的显微结构.结果表明:当分散剂用量为8.74%(质量分数),pH为10.8,有机单体含量为3.1%时,可制得固相体积含量为40%,粘度为610 mPa·s的ZrB2-SiC复合浆料,此时烧结体的断面主要以穿晶断裂为主;凝胶注模成型的坯体内部的有机聚合物网络因高温而完全分解,使素坯的气孔分布较均匀,利于烧结体致密度的提高.
参考文献
| [1] | Omatete O O;Walls C A .G elcasting a new ceramic forming process[J].Journal of American Ceramic Society Bulletin,1991,70(10):1641-1649. |
| [2] | Janney Mark A;Omatete O O .Method for molding ceramics powders using a water-based gel-casting process[P].US 5145908 |
| [3] | Omatete O O;Janney M A;Nunn S D .Gel-casting from laboratory development toward industrial production[J].Journal of the European Ceramic Society,1997,17:407-413. |
| [4] | Gilissen R;Erauw J P;Smolders A et al.Gelcasting,a near net shape technique[J].Materials & Design,2000,21:251-257. |
| [5] | 芦令超,申玉芳,常钧,刘福田,程新,郭建亭.氧化铝陶瓷料浆流变性的研究[J].硅酸盐通报,2003(04):36-40. |
| [6] | Young A C;Omatete O O .Gelcasting of alumina[J].Journal of American Ceramic Society Bulletin,1997,74(03):612-618. |
| [7] | Janney M A .Method for molding ceramic powders[P].US 4894194 |
| [8] | 杨金龙 .陶瓷胶态成形工艺及原位凝固机制的研究[D].清华大学,1996. |
| [9] | 魏文德.有机化工原料大全[M].北京:化学工业出版社,1990:84-96. |
| [10] | 严瑞瑄.水溶性高分子[M].北京:化学工业出版社,1998:84-177. |
| [11] | 钦征骑.新型陶瓷材料手册[M].南京:江苏科学技术出版社,1995:155. |
| [12] | 李世普.特种陶瓷工艺学[M].武汉:武汉工业大学出版社,1990:76. |
| [13] | Annika K .Water-based tape casting of ceramics and fabrication of ceramic laminate[D].Goteborg,Swedish,1999. |
| [14] | 谢志鹏;黄勇;王林 等.氮化硅陶瓷注射成型体脱脂过程的研究[J].现代技术陶瓷,1994,62(04):3-7. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%