在钛酸锶钡(BSTO)与质量分数为60%的MgO混合的基础上,研究了MnCO3掺杂对BSTO/MgO复相铁电陶瓷介电性能的影响.随着MnCO3掺杂量的增加,BSTO晶粒尺寸减小.适量的MnCO3的掺杂可明显降低BST/MgO复相材料的高频损耗以及显著提高材料的调谐性.当MnCO3掺杂量为0.5%(物质的量分数)时,BSTO/MgO 材料的介电常数为94,高频损耗为2.91×10-3(4.191 GHz),介电常数可调率达7.4%(2 kV/mm).
参考文献
[1] | Wu L.;Chen Y.C. .Direct-current field dependence of dielectric properties in alumina-doped barium strontium titanate[J].Journal of the American Ceramic Society,2000(7):1713-1719. |
[2] | Synowczynski J;Sengupta L C;Chiu L H.Investigation of the effect of particle size on the 10GHz microwave properties of Ba1-xSrxTiO3/MgO composite ceramics[J].Integrated Ferroelectric,1998(22):341-352. |
[3] | 杨春霞,周洪庆,刘敏,吴红忠,梁斌斌,金宇龙.BSTO/MgO铁电移相材料的研究[J].电子元件与材料,2005(02):13-15. |
[4] | Liou J W;Chiou B S .Effect of direct-current biasing on the dielectric properties of barium strontium titanate[J].Journal of The American Chemical Society,1997,80(12):3093-3099. |
[5] | Jang S J;Amar B .Studying a ferroelectric at microwave frequencies[J].Ferroelectrics,1988,87:303-308. |
[6] | 关振铎;张中太;焦金生.无机材料物理性能[M].北京:清华大学出版社,1992:248. |
[7] | Negas T .BaTi4O9/Ba2Ti9O20 based ceramics resurrected for modern microwave applications[J].American Ceramic Society of Bulletin,1993,72(01):80-89. |
[8] | 吴顺华,陈力颖,陈晓娟,赵玉双,张志萍,熊文.Mn掺杂BaTi4O9陶瓷结构和介电性能[J].硅酸盐学报,2001(01):80-83. |
[9] | 姜胜林;王筱珍;张绪礼 .MnO对改性钛酸铅陶瓷压电性能的影响[J].电子元件与材料,1995,14(01):34-36. |
[10] | Lee S G;Kim C Il;Kim J P.Structural and dielectric properties of barium strontium calcium titanate thick films modified weith MnO2 for phased array antennas[J].Materials Letters,2003(58):110-114. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%