采用注凝成型技术研究了Y2O3浆料的流变性能.研究发现,浆料的粘度与分散剂的加入量有密切关系.分散剂加入量为5%～8%(质量分数),固体含量为60%(体积分数),球磨时间控制在20～26 h时,浆料粘度为0.4～0.6Pa·s,达到最佳分散状态.
参考文献
| [1] | 黄振国,修稚萌,孙旭东.不添加烧结助剂制备透明的Y2O3陶瓷[J].材料研究学报,2004(04):399-404. |
| [2] | 闻雷,孙旭东.碳酸盐前驱物制备Y2O3超细粉及透明陶瓷[J].中国稀土学报,2003(02):166-169. |
| [3] | Greskovich C;Woods K N .Fabrication of transparent ThO2-doped Y2O3[J].J Am Ceram So,1973,52(05):473-477. |
| [4] | 闻雷,孙旭东,王介强,左良.Y2O3超微粉及其透明陶瓷的制备[J].东北大学学报(自然科学版),2002(12):1151-1154. |
| [5] | Omatete Ogbemi O;Aler B .Evaluation of dispersants for gel-casting of alumina[J].Dispersion Aggregation Proc Eng Found Conf,1994,7:269-278. |
| [6] | Jenny M A;Omatete O O .[P].US 5145908,1992. |
| [7] | Jenny M A .[P].US 4894194,1990. |
| [8] | Jenny M A;Omatete O O .[P].US 5028362,1991. |
| [9] | Omatete O O;Pollinger J P.G elcasting and aquous injection molding for silicon nitride structural ceramics[A].USA:Materials Reserch Laboratory at UCSB,1997:11. |
| [10] | Anderson P J .Zeta potentials in relation to rheological properties of oxide slips[J].Journal of The American Chemical Society,1975,42(02):70-74. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%