采用相图分析了中间包溶渣对于式振动料的侵蚀机理,并用扫描电镜、能谱及X-ray衍射对中间包干式振动料残衬进行显微观察和分析.结果表明:在中间包使用初期,熔渣对中间包工作衬侵蚀的途径为渗透;在渗透的同时,熔渣对干式料产生化学侵蚀及干式料对熔渣产生化学过滤作用、方镁石溶于熔渣改变了熔渣的性质,提高了熔渣的熔点和粘度,在干式振动料/熔渣界面形成致密的结构,阻碍熔渣的进一步渗透;此后,熔渣对干式料侵蚀的主要途径是对界面致密层的溶蚀.
参考文献
| [1] | Zhang S;Sarpoolaky H;Marriott N J et al.Penestration and corrosion of magnesia grain by silicate slags[J].British Ceramic Transactions,2000,99(06):248-255. |
| [2] | 贺智勇,李林,曹铁柱.减少中间包渣在涂料中渗透的途径[J].钢铁,2002(06):51-53. |
| [3] | KUSUHIRO MUKAI;ZAINAN TAO;KIYOSHI GOTO .In-situ X-ray Observation and Microstructural Analysis on Slag Penetration into MgO Refractories[J].Taikabutsu Overseas,2001(1):3-10. |
| [4] | 王维邦.耐火材料工艺学[M].北京:冶金工业出版社,1994 |
| [5] | 王俭;毛裕文.渣图集[M].北京:冶金工业出版社,1989 |
| [6] | Cho M K;Hong G G;Lee S K .Corrosion of spinel clinker by CaO-Al2O3-SiO2 ladle slag[J].Journal of the European Ceramic Society,2002,22(11):1783-1790. |
| [7] | 郁国城.碱性耐火材料理论基础[M].上海:上海科学技术出版社,1982:2. |
| [8] | Nakagawa H;Nakamura Y;Sawano K.Development of MgO-CaO-Al2O3 castable for steel ladle slag line[A].,1997:475-480. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%