以Y2O3为基质材料,掺杂不同含量的La3+,采用高能球磨法制备出性能良好的La0.2Y1.8O3纳米粉.对不同球磨时间后的粉体进行了X射线衍射、透射电镜和比表面积等分析.结果表明:La3+完全固溶于Y2O3的立方晶格中,La0.2Y1.8O3粉体大小均匀,近似球形,且随着球磨时间延长,其颗粒逐渐变小,晶格畸变增加;900℃煅烧2h的粉末尺寸约40～60 nm左右.1650℃真空烧结3h后,得到了La0.2Y1.8O3透明陶瓷.
参考文献
| [1] | Lu J;Prabhu M;Song J et al.Optical properties and highly efficient laser osciuation of Nd:YAG ceramics[J].Appl B,2000,71(04):469-473. |
| [2] | Kazunori Takaichi;Hideki Yagi;Jianren Lu;Jean-Francois Bisson;Akira Shirakawa;Ken-ichi Ueda;Takagimi Yanagitani;Alexander A. Kaminskii .Highly efficient continuous-wave operation at 1030 and 1075 nm wavelengths of LD-pumped Yb~(3+):Y_(2)O_(3) ceramic lasers[J].Applied physics letters,2004(3):317-319. |
| [3] | Saito N.;Ikegami T.;Matsuda S. .Fabrication of transparent yttria ceramics at low temperature using carbonate-derived powder[J].Journal of the American Ceramic Society,1998(8):2023-2028. |
| [4] | 闻雷,孙旭东,其鲁,徐国祥.湿化学法制备Y2O3纳米粉及透明陶瓷[J].无机材料学报,2006(03):539-546. |
| [5] | 王晓慧.BaTiO3纳米晶的合成与表征[J].高等学校化学学报,1994(02):159. |
| [6] | 魏诗榴.粉体机械力化学[M].广州:华南理工大学出版社,1986 |
| [7] | 陈鼎,严红革,黄培云.机械力化学技术研究进展[J].稀有金属,2003(02):293-298. |
| [8] | 吴其胜,高树军,张少明,杨南如.BaTiO3纳米晶机械力化学合成[J].无机材料学报,2002(04):719-724. |
| [9] | 范恩荣.钛酸钡超细粉合成途径探讨[J].电瓷避雷器,2000(06):16-20. |
| [10] | 杨秋红,徐军,苏良碧,张红伟.Yb：Y2-2xLa2xO3激光透明陶瓷的光谱性能[J].物理学报,2006(03):1207-1210. |
| [11] | 刘军芳,傅正义,张东明,张金咏.透明陶瓷的制备技术及其透光因素的研究[J].硅酸盐通报,2003(03):68-73. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%