研究了烧成温度和保温时间对添加活性氧化铝的红柱石基耐火材料莫来石化行为的影响.对试样XRD数据的分析结果表明,烧成温度升高,莫来石含量线性增大,残存红柱石线性减少,二者具有良好的相关性.氧化铝溶解入液相主要在1400℃之前.二次莫来石化反应主要发生在1500℃之后.1600℃烧成时,保温3h之内,莫来石含量增长速度最快.二次莫来石的生成反应在一定程度上滞后于一次莫来石反应和刚玉溶解入液相的反应.
参考文献
| [1] | 扬直夫 .红柱石--生产优质耐火材料用最有前途的材料[J].国外耐火材料,2001,26(03):32-37. |
| [2] | Ildefonse J P;Gabis V;Rigaud M.Mullitization of andalusite in bricks and castables[A].The American Ceramic Society,Westerville,1997:899-908. |
| [3] | J.P.Ildefonse;V.Gabis;F.Cesbron .Mullitization of andalusite in refractory bricks[J].Key engineering materials,1997(3):1798-1801. |
| [4] | Hülsmann A;Schmücker M;Mader W et al.The transformation of andalusite to mullite and silica:Part Ⅱ.transformation mechanisms in[100]and[010] Directions[J].American Mineralogist,2000,85(7-8):987-992. |
| [5] | Bouchetou M L;Ildefonse J P;Poirier J et al.Mullite grown from fired andalusite grains:the role of impurities and of the high temperature liquid phase on the kinetics of mullitization and consequences on thermal shocks resistance[J].Ceramics International,2005,31:999-1005. |
| [6] | Marie Laure Bouchetou;Jean Pierre Ildefonse;Jacques Poirier .Production of a high mullite content material from natural andalusite:influence of grain size[J].Refractories Applications and News,2005,10(05):21-25;31. |
| [7] | 文洪杰;苗圃;李文超 .红柱石的莫来石化动力学[J].耐火材料,1995,29(03):140-141;148. |
| [8] | 廖桂华,徐国辉,李柳生,蒋明学.烧成温度和保温时间对红柱石基材料烧结性能的影响[J].耐火材料,2005(04):255-258. |
| [9] | 李柳生,平增福.红柱石的莫来石化[J].硅酸盐通报,2006(01):34-36. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%