系统地介绍了MgO-CaO-ZrO2耐火材料的性能特点、应用领域、制备与使用情况.指出,利用高纯原料制备MgO-CaO-ZrO2耐火材料已取得成功,而利用天然原料低成本地制备MgO-CaO-ZrO2耐火材料将成为今后研究的主要课题;同时指出,MgO-CaO-ZrO2耐火材料的剥落现象是影响其使用寿命的主要原因,还有待于进一步研究改进.
参考文献
| [1] | 王诚训;张义先;于青.ZrO2复合耐火材料[M].北京:冶金工业出版社,1997 |
| [2] | 陈肇友.从相图讨论MgO-CaO-ZrO2耐火材料抗炉外精炼渣与水泥的侵蚀[J].耐火材料,2002(02):107-110. |
| [3] | Hisao Kozuka.Further improvement of MgO-CaO-ZrO2 bricks for burning zone of rotary cement kiln[A].:256-263. |
| [4] | Christopher L Macey .Refractory solutions for high wear in cement kiln transition zones[A].New Orleans,Louisiana,USA,3:1625-1631. |
| [5] | 孙加林;洪彦若;窦叔菊 .耐火材料的显微结构分析[J].耐火材料,1996,30(05):255-258. |
| [6] | 徐延庆,叶国田.水泥回转窑用含ZrO2耐火材料[J].耐火材料,2003(02):105-107. |
| [7] | Glyn Cox .Selecting refractory materials[J].WORLD CEMENT,2000,31:48-56. |
| [8] | Hisao Kozuka;Yoshiharu Kajita;Yoshiki Tuchiya.New kind of chrome-free Mgo-Cao-ZrO2 bricks for burning zone of rotary kiln[A].:1027-1037. |
| [9] | Hisao Kozuka;Yoshiharu Kajita;Kozo Tokunaga.Further improvement of MgO-CaO-ZrO2 refractory bricks[J].WORLD CEMENT,1996:32-34. |
| [10] | 李鑫.水泥回转窑用MgO-CaO-ZrO2砖的改进[J].国外耐火材料,1996(08):25-28. |
| [11] | FUMIHITO OZEKI;YOSHIHARU KAJITA;TORU HONDA .Chrome-Free Basic Bricks for Cement Rotary Kilns[J].Taikabutsu Overseas,2001(2):78-84. |
| [12] | 王华;王杰曾;夏霞云 等.水泥窑用烧成富镁白云石砖抗热震性的研究[J].耐火材料,1999,33(05):250-253. |
| [13] | 廖建国.水泥回转窑用无铬砖的演变[J].国外耐火材料,2003(05):6-10. |
| [14] | 张干通,张保玉,张素芳.镁钙锆砖在新型干法回转窑烧成带的应用[J].新世纪水泥导报,2001(04):32. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%