以脱硅锆、白云石生料以及轻烧氧化镁为原料,研究了n(CaO):n(ZrO2)分别为0.8、0.9、1.0、1.1时对MgO-ZrO2-CaO合成料结构和性能的影响.结果发现:当配料中n(CaO):n(ZrO2)＜1时,合成料中未发现有游离的ZrO2存在,且合成料中可生成CaZrO3和CaZr4O9两种锆酸钙相;随着配料中ZrO2含量的增加,合成料中方镁石和锆酸钙相呈现不同的分布特征;n(CaO):n(ZrO2)的提高有利于改善合成料的烧结性能;在合成料中,杂质成分主要以硅酸盐相存在,以孤岛状分布于锆酸钙颗粒的角隅之间,对合成料的烧结性能和高温性能没有太大影响.
参考文献
| [1] | Fumihito O .Chrome-free basic brick for cement rotary kiln[J].Taikabutsu,1999,51(02):83-84. |
| [2] | Uwe B.Experience with a new generation of chrome-free magnesiaenriched dolomite bricks in cement kilns[A].:1605-1611. |
| [3] | Chritopher L,Macey.Refractory solutions for high wear in cement kiln transition zones[A].:1625-1631. |
| [4] | Ozeki F .New magnesia - spinel bricks for cement rotary kiln utilizing waste in large quality[J].Taikabutsu,2000,52(01):28-30. |
| [5] | Komatsu H .The development of magnesia - spinel brick with high resistance against alkali salts in cement rotary kiln[J].Taikabutsu,2000,52(02):78-87. |
| [6] | Glyn C.Selecting refractory materials[J].World Cement,2000(03):48-56. |
| [7] | Glyn C.Selecting refractory materials[J].World Cement,2000(04):76-82. |
| [8] | 郁国城.碱性耐火材料理论基础[M].上海:上海科学技术出版社,1982:221-231. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%