以电熔白刚玉、α-Al2O3、锐钛矿和单质Si为原料,固定配料中电熔白刚玉和α-Al2O3的质量分数分别为80%和20%,锐钛矿的外加量为6%,分别外加0、 2%、4%和6%的单质Si,经混练、成型、干燥后在空气气氛中于1550 ℃保温3 h烧成,检测烧后试样的显气孔率、体积密度、耐压强度、抗折强度和线变化率,并采用XRD分析烧后试样的相组成.结果表明:在刚玉材料中同时加入锐钛矿和单质Si能降低材料的显气孔率,提高材料的抗折强度和耐压强度,并有钛酸铝和莫来石生成;另外,单质Si对材料中的钛酸铝具有较好的稳定作用,但随着单质Si含量由2%增加至6%,材料中的钛酸铝含量减少,莫来石含量增加.
参考文献
| [1] | Sepulveda P;Studart A R;Pandolfelli V C et al.Characterization and properties of refractory grade bauxites[J].International Ceram:International Ceramic Review,1999,48(06):398-406. |
| [2] | Victor Valcarcel;Carmen Cerecedo;Francisco Guitian .Method for Production of α-Alumina Whiskers via Vapor-Liquid-Solid Deposition[J].Journal of the American Ceramic Society,2003(10):1683-1690. |
| [3] | 吴振东,叶建东.添加剂对氧化铝陶瓷的烧结和显微结构的影响[J].兵器材料科学与工程,2002(01):68-72. |
| [4] | J. DENG;T. CAN;J. SUN .Microstructure and mechanical properties of hot-pressed Al_2O_3/TiC ceramic composites with the additions of solid lubricants[J].Ceramics International,2005(2):249-256. |
| [5] | 郭玉香,曲殿利,张芸.钛酸铝对刚玉质耐火材料性能的影响[J].耐火材料,2002(06):351-352. |
| [6] | Uribe R;Baudin C .Alumina-aluminium titanate composites with improved thermal shock resistance[J].Key Engineering Materials,2001,206-213:1041-1044. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%